Korepox H.B-EH270 Epoxy Paint is an epoxy paint. Parameters on this page: volume solids approx. 55% (determined per ISO 3233), dry film thickness 100 µm (single coat), theoretical spreading rate 5.5 m²/L/100 µm. Comparable products of the same brand: KOREPOX EH2350 Modified High-solids Epoxy Paint, KOREPOX EP174 Epoxy Abrasion-resistant Paint, Korepox H.B. EH2560 Epoxy Paint.
Data source: KCC original Technical Data Sheet (TDS), "Korepox H.B (Heavy-duty Anti-corrosion) -EH270 Epoxy Paint"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | approx. 55% |
|---|---|
| Dry Film Thickness | 100 µm (in one coat) |
| Theoretical Spreading Rate | 5.5 m²/L /100 µm |
| VOC | — |
| Density / Specific Gravity | 1.2–1.4 kg/L (after mixing, depending on colour) |
| Number of Components | Two-component |
| Thinner | No. 024 (within a maximum of 20%, by volume) |
| Colour / Appearance | Flat, white (1000), grey (1128), brown (2282) |
| Packaging Specifications | 16 L pack (EH270PTA: 12.8 L, EH270PTB: 3.2 L) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Korepox H.B. EH270 is a high-build two-component paint with polyamide-cured epoxy resin as the main component, with excellent abrasion and impact resistance. Excellent water and salt water resistance, and strong resistance to petroleum (gasoline), diesel, lubricating oils and other similar substances, but limited resistance to ketones and esters. This product is not suitable for strongly oxidizing solutions such as mineral acids.
For intermediate coat or finish on steel in severely corrosive environments at non-permanently immersed locations.
| Appearance and colour | Flat, white (1000), grey (1128), brown (2282) |
|---|---|
| density | Mixture, depending on colour, approx. 1.2–1.4 |
| Volume Solids | approx. 55% (determined per ISO 3233) |
| Theoretical Spreading Rate | On a smooth surface, dry film thickness 100 µm, 5.5 m²/L |
| Flash Point | Base (EH270PTA): 26 °C (closed cup); hardener (EH270PTB): 29 °C (closed cup) |
*Iron: blast clean to Sa 2.5 "near-white blast cleaning". Can be applied directly to the substrate, or apply Korepox Zinc Rich Primer EZ175 or a suitable anti-corrosive primer first. *Concrete: treat the substrate surface with a 3% solution of hydrochloric acid or phosphoric acid and dry; thin with Thinner No. 024 (10–15%) for a sealing coat.
Spray (air spray or airless spray). Airless spray: nozzle tip size 432–584 µm (0.017–0.023 in); spray pressure 11.7–15.2 MPa; spray angle 40°–60°.
Base (EH270PTA) : Hardener (EH270PTB) = 4 : 1 (by volume). Mix the components completely in the specified ratio 30 minutes before application.
Thinner No. 024 (within a maximum of 20%, by volume). Do not thin the components separately; only thin the mixture.
Application and curing temperature above 5 °C is most suitable; the surface must be clean and dry. The surface temperature of the object to be coated shall be at least 3 °C above the dew point. Relative humidity 40–60% is most suitable; avoid application when it exceeds 85%.
1 coat: dry film thickness 100 µm. The film thickness can be adjusted according to the application location and use.
| Substrate temperature | 5°C | 20°C | 30°C |
|---|---|---|---|
| Touch dry | 8 h | 4 h | 2 h |
| Curing/drying | 48 h | 18 h | 12 h |
Korepox Top Coat ET574, ET5740, ET5745 or according to the coating specification.
4 h at 20 °C.
At 20 °C, minimum 16 hours, maximum 30 days.
Continuous: 93 °C; intermittent: 121 °C.
| Shelf life | 12 months |
|---|---|
| Packaging Specifications | 16 L pack (EH270PTA: 12.8 L, EH270PTB: 3.2 L) |
Prevent this product from directly contacting skin and eyes; avoid prolonged inhalation of solvent vapours. Ensure adequate ventilation during application; wear respiratory protective equipment when working in enclosed spaces. Date of issue: 2012-08-01.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.