KOREPOX EH2350 Modified High-solids Epoxy is an epoxy coating. Parameters on this page: volume solids approx. 80% (determined per ISO 3233), dry film thickness 150 µm (maximum per application), theoretical spreading rate 8.0 m²/L/100 µm. Comparable products from the same brand: KOREPOX EH2350 Modified High-solids Epoxy, KOREPOX EP174 Epoxy Abrasion-resistant, Korepox H.B. EH2560 Epoxy.
Source: KCC original technical data sheet (TDS) "KOREPOX EH2350 (WM) Modified High-solids Epoxy"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 80% |
|---|---|
| Dry Film Thickness | 150 µm (maximum per application) |
| Theoretical Spreading Rate | 8.0 m²/L at 100 µm |
| VOC | — |
| Density / Specific Gravity | 1.4–1.7 kg/L (after mixing, by colour) |
| Number of Components | Two-component |
| Thinner | No. 024 (by volume) |
| Colour / Appearance | Flat, white, or as required |
| Packaging Specifications | 16 L pack (EH2350(WM)-A: 12.8 L, EH2350(WM… |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
KOREPOX EH2350 (WM) is a polyamide-cured two-component high-solids high-build paint based on fatty-acid-modified epoxy resin, with good water resistance and rust prevention, suitable as a special paint for wind-turbine towers. This product is not recommended for use in contact with acid or oxidising solutions.
A special intermediate coat for onshore and offshore wind-turbine towers, used in a system with a polyurethane topcoat under exterior exposure.
| Appearance and colour | Flat, white, or as required |
|---|---|
| density | Mixture, by colour, 1.4–1.7 |
| Volume Solids | Approx. 80% (determined per ISO 3233) |
| Theoretical Spreading Rate | On smooth surfaces, 150 µm dry film thickness, 5.33 m²/L |
| Flash Point | Base EH2350(WM)-A: 23 °C (closed cup); curing agent EH2350(WM)-B: 27 °C (closed cup) |
Remove oil, dust and other contaminants from the previously coated substrate surface.
EPOXY ZINC RICH PRIMER EZ175(WM), or per the coating specification.
Thinner No. 024 (by volume). The two components must not be thinned separately; only the mixture may be thinned.
The surface to be coated shall be completely clean and dry. Relative humidity must not exceed 85%, and the surface temperature shall be at least 2.7 °C (5 °F) above the dew point to avoid condensation. When working in enclosed spaces, provide clean circulating air to aid solvent evaporation.
Maximum dry film thickness per application: 150 µm. The recommended film thickness varies with use and coated area; the maximum film thickness varies with thinning ratio and application method.
| Substrate Temperature | 5°C/41℉ | 20°C/68℉ | 30°C/86℉ |
|---|---|---|---|
| Touch Dry | 12 h | 6 h | 4 h |
| Hard Dry | 48 h | 24 h | 28 h |
Polyurethane topcoat, or per the coating specification.
20 °C, 4 h.
At 20 °C/68 °F, minimum 18 h; maximum 7 days with polyurethane topcoat.
Continuous: 93 °C (non-immersed); intermittent: 121 °C (non-immersed).
| Shelf life | 12 months |
|---|---|
| Packaging Specifications | 16 L pack (EH2350(WM)-A: 12.8 L, EH2350(WM)-B: 3.2 L) |
Do not store at temperatures below 5 °C/41 °F or above 40 °C/104 °F. Protect skin and eyes from direct contact with liquid coating, and avoid prolonged inhalation of solvent vapours. Issue date: 2010-06-01; revision date: 2015-09-01.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.