KOREPOX EP174 Epoxy Abrasion-resistant Coating belongs to Epoxy. Parameters on this page: volume solids approx. 52% (determined to ISO 3233), dry film thickness 125 µm (single coat), theoretical spreading rate 5.2 m²/L/100 µm. Comparable models from the same brand: KOREPOX EH2350 Modified High-solids Epoxy, KOREPOX EP174 Epoxy Abrasion-resistant Coating, Korepox H.B. EH2560 Epoxy.
Parameter source: KCC original technical data sheet (TDS) 'KOREPOX EP174 Epoxy Abrasion-resistant Coating'; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 52% |
|---|---|
| Dry Film Thickness | 125 µm (single application) |
| Theoretical Spreading Rate | 5.2 m²/L/100 µm |
| VOC | — |
| Density / Specific Gravity | 1.3–1.5 kg/L (mixed, depending on colour) |
| Number of Components | Two-component |
| Thinner | No.024 (max. 20% by volume) |
| Colour / Appearance | Flat, white (1000), grey (1128), cream (3332) |
| Packaging Specifications | 16 L pack (EP174PTA: 12 L, EP174PTB: 4 L) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
KOREPOX EP174 is a two-component amine adduct-cured epoxy resin-based coating with good abrasion resistance and impact resistance. With a suitable topcoat, the product is suitable for steel structures.
Intermediate coat or topcoat for cargo warehouses; suitable as a primer on steel structures.
| Appearance and colour | Flat, white (1000), grey (1128), cream (3332) |
|---|---|
| density | Mixture, approx. 1.3–1.5 depending on colour |
| Volume Solids | Approx. 52% (determined to ISO 3233) |
| Theoretical Spreading Rate | On smooth surfaces, at dry film thickness 125 µm, 4.16 m²/L |
| Flash Point | Base (EP174PTA): 26°C (closed cup); Hardener (EP174PTB): 26°C (closed cup) |
Remove all oil, grease, dust and other contaminants from the surface to be coated before application. Steel: blast clean to Sa2.5 or power tool clean to St3.
When used as intermediate coat or topcoat, apply as required over GALVANY IZ180(N), KOREPOX HOLDING PRIMER EP170, or per the coating specification.
Brush application or spray (conventional or airless). Airless spray: nozzle tip size 483-686 µm (0.019″-0.027″); nozzle pressure 11.7-15.2 MPa; spray angle 40°-60°.
Base (EP174 PTA): Hardener (EP174 PTB) = 3:1 (by volume). Thoroughly mix the two components in the specified ratio 30 min before application.
Thinner No.024 (max. 20% by volume). Do not thin the two components separately; thin the mixed product only.
Ideal application and curing temperature is above 5°C; the substrate surface shall be clean and dry. Substrate surface temperature shall be at least 3°C above dew point. Ideal relative humidity 40-60%; do not exceed 85%.
Single application: dry film thickness 125 µm. The film thickness may be adjusted according to the coated area and purpose.
| Substrate temperature | 5°C | 20°C | 30°C |
|---|---|---|---|
| Touch dry | 8 h | 2 h | 1 h |
| Curing/drying | 72 h | 16 h | 14 h |
Per the coating specification.
4 h at 20 °C.
At 20°C, minimum 8 h; maximum 1 month (when recoating with itself), 3 months (when applying an epoxy topcoat).
Continuous: 93 °C; intermittent: 121 °C.
| Shelf life | 12 months |
|---|---|
| Packaging Specifications | 16 L pack (EP174PTA: 12 L, EP174PTB: 4 L) |
Prevent contact of the product with skin and eyes; avoid prolonged inhalation of solvent vapour. Provide adequate ventilation during application; wear respiratory protection when applying in confined spaces. Prolonged exposure to sunlight may cause discolouration or chalking. Issue date: 2013-07-01.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.