Korepox EH2350 epoxy glass flake coating is a glass flake coating of the epoxy system. Parameters on this page: volume solids around 80% (determined to ISO 3233), dry film thickness 250 µm, theoretical spreading rate 8.0 m²/L/100 µm. Comparable products from the same brand: Korepox EH2350 epoxy glass flake coating, KOREPOX H.B EH3200 epoxy glass flake coating, KOREPOX EH2350 high-build epoxy primer.
Source: KCC original technical data sheet (TDS) 'Korepox EH2350(GF) Epoxy Glass Flake Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 80% |
|---|---|
| Dry Film Thickness | 250 µm |
| Theoretical Spreading Rate | 8.0 m²/L at 100 µm |
| VOC | — |
| Density / Specific Gravity | 1.5 kg/L (after mixing, depending on colour) |
| Number of Components | Two-component |
| Thinner | No.024 |
| Colour / Appearance | Flat, grey (1128) |
| Packaging Specifications | 18 L pack (EH2350(GF)PTA: 14.4 L, EH2350PT… |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Korepox EH2350(GF) is a two-component primer coating based on epoxy resin, reinforced with glass flake, with high seawater and abrasion resistance. It can be sprayed on new substrates, and also over old film once the rust on the material surface is removed at the time of coating. This product can be applied and cured below -18 °C/-0.4 °F, is a high-solids coating free of coal tar, and meets VOC regulations.
Provides long-term protection of steel plates and other structural materials in severely corrosive areas, such as ship bottoms fully immersed in water, ballast tanks, cargo tanks, crude oil tanks, fuel oil tanks and crude oil pipelines. Can also be applied to steel structures in offshore projects, plants and bridges.
| Appearance and colour | Flat, grey (1128) |
|---|---|
| density | Mixture, approx. 1.5 depending on colour |
| Volume Solids | Approx. 80% (measured according to ISO 3233) |
| Theoretical Spreading Rate | On smooth surfaces, 250 µm dry film thickness, 3.2 m²/L |
| Flash Point | Base (EH2350(GF)PTA): 26 °C (closed cup); hardener (EH2350PTB): 26 °C (closed cup) |
Use clean water or an appropriate solvent to completely remove rust, dust, moisture, oil and other contaminants from the substrate surface. ● Steel: blast-clean to at least Sa 2.5 or Sa 2.
Korepox Holding Primer EP170QD, Korepox Holding Primer EP1700, Korepox EH2350, GALVANY IZ182(J)
Apply by roller, brush or spray (air or airless). Airless spray: nozzle tip 635–889 µm (0.025–0.035″); spray pressure 15.1–17.2 MPa; fan width 60°.
Base (EH2350(GF)PTA) : hardener (EH2350PTB) = 4:1 (by volume). Stir each component separately before application, then combine in the ratio and mix thoroughly.
Thinner No. 024. Do not thin the two components separately; thin only the mixture.
The surface to be coated must be completely clean and dry. Relative humidity must not exceed 85%. The surface temperature must be at least 2.7 °C (5 °F) above the dew point to avoid condensation. In winter, keep the substrate and ambient temperature above 10 °C during application, and keep the curing temperature above 5 °C after application.
Dry film thickness: 250 µm. The dry film thickness varies with the intended use and area.
| Substrate temperature | 5°C | 20°C | 30°C |
|---|---|---|---|
| Touch dry | 8 h | 1 h | 30 min |
| Hard Dry | 16 h | 3 h | 2 h |
In accordance with the coating specification.
At 20 °C, 3 h.
At 20 °C, minimum 3 h; maximum: unlimited (non-immersion), 12 days (immersion).
Continuous: 93 °C (non-immersion areas); intermittent: 121 °C (non-immersion areas).
| Shelf life | 12 months |
|---|---|
| Packaging Specifications | 18 L pack (EH2350(GF)PTA: 14.4 L, EH2350PTB: 3.6 L) |
Protect eyes and skin; avoid prolonged inhalation of solvent vapour. Ensure adequate ventilation during application. Keep away from sparks and open flames. Issue date: 2010-06-01.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.