6194A UMEGUARD SX HS QD Epoxy is an epoxy coating. It has excellent physical properties such as strong adhesion, tough film and good abrasion resistance. Parameters on this page: volume solids 77 ± 2% (ISO: 3233), dry film thickness 100–200 µm, theoretical spreading rate 0.13–0.26 L/m². Comparable products from the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Source: CMP original technical data sheet (TDS) "6194A UMEGUARD SX HS QD Epoxy"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 77 ± 2% (ISO:3233) |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.13-0.26 L/m2 |
| VOC | 232 g/L (Method24) |
| Density / Specific Gravity | 1.47 g/mL (ISO:2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
| Colour / Appearance | Black, grey, green, red-brown, and similar |
UMEGUARD SX HS QD is a modified epoxy with low surface preparation requirements. It has excellent physical properties such as strong adhesion, tough film and good abrasion resistance.
It also has excellent seawater corrosion resistance and cathodic protection.
| Type | Epoxy |
|---|---|
| Use | Can be used as an anticorrosive for ship bottoms, cargo holds, the interior and exterior of accommodation spaces, void spaces, cofferdams, machinery rooms, pipelines and other steel structures. Suitable for maintenance and repair. |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
|---|---|
| Colour | Black, grey, green, red-brown, and similar |
| Flash Point | Base 29.2 °C, curing agent 27.2 °C |
| Density | 1.47 g/mL (ISO:2811) |
| Volume Solids | 77 ± 2% (ISO:3233) |
| Volatile organic compound content | 232 g/L (Method24) |
| Theoretical spreading rate | 0.13-0.26 L/m2 |
| Thickness | WFT 130–260 µm, DFT 100–200 µm |
(150 µm dry film) 30 °C
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | |
| Drying Time | Surface Dry | 18 h | 14 h | 9 h | 4 h | 1.5 h |
| Hard Dry | 50 h | 36 h | 22 h | 12 h | 7 h | |
| Recoat interval | At least | 50 h | 36 h | 22 h | 12 h | 7 h |
| At most | 7 days | 7 days | 7 days | |||
| Pot life | 9 h | 7 h | 5 h | 3 h | 1.5 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.5-2.0 Pa.s |
| Nozzle | (Graco)419-623 |
| Paint output pressure | 15-25 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | WELBOND, CERABOND, NZ PRIMER, EPICON ZINC RICH PRIMER |
| Subsequent coat | EPICON MARINE HB, UNY MARINE, etc. |
| Packaging | Two-component |
Note: 1. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
2. Stir the base with a mixer until homogeneous, then add the curing agent and mix with a power mixer. Then add the appropriate amount of thinner and mix.
3. Excessive solvent may reduce sag resistance and film performance.
4. As an inherent property of modified epoxy coatings, UMEGUARD SX HS chalks and fades under UV light.
5. Waiting time before loading the first cargo
| Film thickness/temperature | 10°C | 20°C | 30°C |
| 200 µm (days) | 25 | 16 | 9 |
| 350 µm (days) | 38 | 24 | 14 |
5. VOC content, volume solids and density are theoretical calculated values excluding thinner. Values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.