5056 BANNOH 500 QD Epoxy is an epoxy coating. It has many physical properties such as good adhesion, a tough, abrasion-resistant film, and outstanding applicability, with resistance to seawater and cathodic protection. Parameters on this page: volume solids 63 ± 2%, dry film thickness 100-200 µm, theoretical spreading rate 0.16-0.32 L/m². Comparable models from the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Parameter source: CMP original technical data sheet (TDS) for 5056 BANNOH 500 QD Epoxy; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 63 ± 2% |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.16-0.32 L/m2 |
| VOC | 394 sq/L |
| Density / Specific Gravity | 1.29 g/mL |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
| Colour / Appearance | Light grey, grey, red-brown |
MARINE PAINTS.!
| Type | Epoxy |
|---|---|
| Use | For anti-corrosion of hull shell, superstructures, external decks and ballast tanks |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
|---|---|
| Colour | Light grey, grey, red-brown |
| Flash Point | Base 23.1 °C, curing agent 24.9 °C |
| Density | 1.29 g/mL |
| Volume Solids | 63±2% |
| Volatile organic compound content | 394 sq/L |
| Theoretical spreading rate | :0.16-0.32 L/m2 |
| Thickness | WFT 159–317 µm |
| Dry film | 100–200 µm |
(dry film 200 µm)
| Temperature | -5°C | 0°C | 5°C | 10°C | 20°C | |
| Drying Time | Surface Dry | 10 h | 7 h | 5 h | 4.5 h | 3 h |
| Hard Dry | 36 h | 24 h | 17 h | 13 h | 8 h | |
| Recoat interval | At least | 36 h | 24 h | 17 h | 13 h | 8 h |
At most*
| Pot life | 10 h 8 h 6 h 5 h 2 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.6-2Pa.s |
| Nozzle | Graco623,621 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0-13% by volume |
| Preceding coat | CERABOND 2000, EPICON ZINC RICH PRIMER B-2, etc. |
| Subsequent coat | BANNOH 500 N, SILVER SQ-K, EPICON MARINE HB, EPICON FINISH HB, etc. |
| Packaging | Two-component |
Note: 1. * Results from discussion with the CMP sales department. 2. In confined spaces or limited spaces at low temperatures, ventilation equipment is necessary to remove volatilised solvent and promote film formation during application and film formation.
3. Excessive solvent may reduce sag resistance. 4. Application is possible down to -5 °C, but hard dry takes a long time, and full cure is achieved only as the temperature rises.
| 5 | Waiting time before loading the first cargo |
|---|
| Temperature | 5°C | 10°C | 20°C |
| (days) | 25 | 16 | 10 |
6. Volatile organic compound content is a theoretical value calculated for a representative colour formulation (grey) without thinner. The values differ for formulations of different colours.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.