5006 ALP 500 Epoxy Paint is an epoxy coating. It has high adhesion to aluminium surfaces and very good saltwater resistance, workability and high-build application. Parameters on this page: volume solids 58 ± 2%; dry film thickness 50–125 µm; theoretical spreading rate 0.086–0.216 L/m². Comparable products from the same brand: 5055 BANNOH 500 Epoxy Paint, 5055D BANNOH 500 AC Epoxy Paint, 5056 BANNOH 500 QD Epoxy Paint.
Source: CMP original technical data sheet (TDS) '5006 ALP 500 Epoxy Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 58 ± 2% |
|---|---|
| Dry Film Thickness | 50–125 µm |
| Theoretical Spreading Rate | 0.086-0.216 L/m2 |
| VOC | 410 g/L |
| Density / Specific Gravity | 1.24 g/mL |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 66:34 (by volume) |
| Colour / Appearance | Light grey |
ALP 500 is an epoxy primer applied to aluminium hulls, superstructures and other aluminium parts of ships. It has high adhesion to aluminium surfaces and very good saltwater resistance, workability and high-build application.
| Type | Epoxy |
|---|---|
| Use | A primer for aluminium surfaces |
| Mixing Ratio | Base : curing agent = 66:34 (by volume) |
|---|---|
| Colour | Light grey |
| Flash Point | Base 22.5 °C, hardener 26.5 °C |
| Density | 1.24 g/mL |
| Volume Solids | 58 ± 2% |
| Volatile organic compound content | 410 g/L |
| Theoretical spreading rate | 0.086-0.216 L/m2 |
| Thickness | Wet film 86–216 µm |
| Dry film | 50–125 µm |
( )
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3.5 h | 2.5 h | 1.5 h | 1 h |
| Hard Dry | 38 h | 28 h | 16 h | 12 h | |
| Recoat interval | At least | 24 h | 18 h | 10 h | 8 h |
At most*
| Pot life | 24 h, 18 h, 12 h, 8 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | 5°C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 170 s (Ford Cup #4) |
| Nozzle | Graco719,721 |
| Paint output pressure | 14.7-17.7Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | - |
| Subsequent coat | UNY MARINE, VINYL AC-HB, etc. |
| Packaging | Two-component |
Note: 1. *Refer to the coating specification. 2. From application until full cure, maintain ventilation to remove residual solvent and promote curing.
3. Stir the base with a stirrer until uniform, then add the curing agent and mix with a powerful stirrer. Finally add an appropriate thinner and mix.
4. Density and VOC content are calculated without thinner. Values may vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.