6167 UMEGUARD MT Surface-Tolerant Special Epoxy Polyamide Paint is an epoxy coating. The product has excellent tolerance to steel surface conditions, and has excellent anticorrosive, acid and alkali resistance. Parameters on this page: volume solids 82 ± 2%, dry film thickness 100-200 µm, theoretical spreading rate 0.122-0.244 L/m². Comparable models from the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Parameter source: CMP original technical data sheet (TDS) for 6167 UMEGUARD MT Surface-Tolerant Special Epoxy Polyamide Paint; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 82 ± 2% |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.122-0.244 L/m2 |
| VOC | 144 g/L |
| Density / Specific Gravity | 1.50 g/ml |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 80:20 (by volume) |
| Colour / Appearance | Red-brown, light grey |
UMEGUARD MT is a high-solids modified epoxy paint. Specifically designed for application to steel surfaces cleaned by high-pressure fresh water washing. It can be applied when the surface is not thoroughly dry or has slight moisture.
The product has excellent tolerance to steel surface conditions, and has excellent anticorrosive, acid and alkali resistance.
| Type | Surface-Tolerant Special Epoxy Polyamide |
|---|---|
| Use | It can be used as a protective coating for decks, accommodation exteriors, the above-water part of the hull, ballast tanks and other steel structures. |
| Mixing Ratio | Base : curing agent = 80:20 (by volume) |
|---|---|
| Colour | Red-brown, light grey |
| Flash Point | Base: 34.6 °C, curing agent: 97.7 °C, mixture: 37.0 °C |
| Density | 1.50 g/ml |
| Volume Solids | 82 ± 2% |
| Volatile organic compound content | 144 g/L |
| Theoretical spreading rate | 0.122-0.244 L/m2 |
| Thickness | Wet film 122-244 µm; dry film 100-200 µm |
(dry film 250 µm)
| Temperature | 20 °C | 30 °C | 40 °C | |
| Drying Time | Surface Dry | 14 h | 10 h | 6 h |
| Hard Dry | 18 h | 14 h | 9 h | |
| Recoat interval | At least | 24 h | 16 h | 12 h |
| At most | 10 days | 7 days | 5 days | |
| Pot life | 4 h | 3 h | 2 h | |
| Minimum launching time | 6 days | 4 days | 3 days | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 15 °C |
| Humidity | Maximum 95% RH |
| Airless spray: viscosity | 1.5-2.5 Pa.s |
| Nozzle | (Graco)621-623 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | CERABOND 2000, EPICON ZINC RICH PRIMER B-2 |
| Subsequent coat | UMEGUARD MT |
| Packaging | Two-component |
Note: 1. As a pure epoxy resin paint, UMEGUARD MT will inevitably chalk and fade when exposed to ultraviolet light.
2. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
3. Volatile organic compound content and density are theoretical values calculated without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.