6037B EPICON T-800 QD High-build Epoxy Phenolic Tank Lining belongs to Epoxy. A single coat by airless spray can achieve a dry film thickness of 75–160 µm. Parameters on this page: Volume Solids 65 ± 2% [by volume] (ISO:3233), Dry Film Thickness 75–160 µm, Theoretical Spreading Rate 0.115–0.246 L/m². Comparable models from the same brand: 6033 EPICON T-800 HS High-build Epoxy Phenolic Tank Lining, 6037 EPICON T-800 High-build Epoxy Phenolic Tank Lining, 6035 EPICON T-800 HOLDING PRIMER Epoxy Phenolic Resin Temporary Anti-corrosive Primer.
Parameter source: CMP original technical data sheet (TDS) “6037B EPICON T-800 QD High-build Epoxy Phenolic Tank Lining”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 65 ± 2% [by volume] (ISO 3233) |
|---|---|
| Dry Film Thickness | 75–160 µm |
| Theoretical Spreading Rate | 0.115-0.246 L/m2 |
| VOC | 359 g/L (Method 24) |
| Density / Specific Gravity | 1.36 g/ml (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER B |
| Mixing Ratio | Base : curing agent = 84:16 (by volume) |
| Colour / Appearance | Grey, light grey, red-brown |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
EPICON T-800 QD is a high-build epoxy phenolic coating with excellent physical properties such as strong adhesion, tough film and abrasion resistance, and with excellent chemical resistance to salt water, fresh water, petroleum products, crude oil, alkaline substances and weak acids. Suitable as a protective coating for tank interiors. A single coat by airless spray can achieve a dry film thickness of 75–160 µm. Can be applied at low temperatures.
| Type | High-Build Epoxy Phenolic Tank Coating |
|---|---|
| Use | Suitable as a topcoat for oil tanks, chemical tanks and the like |
| Mixing Ratio | Base : curing agent = 84:16 (by volume) |
|---|---|
| Colour | Grey, light grey, red-brown |
| Flash Point | Base 17.5 °C, curing agent 7.5 °C |
| Density | 1.36 g/ml (ISO: 2811) |
| Volume Solids | 65 ± 2% [by volume] (ISO 3233) |
| Volatile organic compound content | 359 g/L (Method 24) |
| Theoretical spreading rate | 0.115-0.246 L/m2 |
| Thickness | WFT 115–246 µm, DFT 75–160 µm |
(dry film 125 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | |
| Drying Time | Surface Dry | 36 h | 16 h | 3.5 h | 2 h | 1 h |
| Hard Dry | 156 h | 78 h | 24 h | 20 h | 8 h | |
| Recoat interval | At least | 156 h | 78 h | 24 h | 20 h | 16 h |
| At most* | 28 days | 28 days | 21 days | 14 days | ||
| At most** | 10 days | 10 days | 7 days | |||
| Pot life | 20 h | 12 h | 8 h | 6 h | 3 h | |
| Induction Time | 120 min | 60 min | 30 min | 20 min | 10 min | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 10 °C |
| Humidity | Maximum 85% RH; steel temperature at least 5 °C above the dew point |
| Airless spray: viscosity | 1.0-1.8Pa.S |
| Nozzle | Graco619, 621, 623 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER B |
| Thinning | 0–10% by volume |
| Newbuilding | Follow the shipyard standards. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil, grease and the like. Remove salts and other contaminants with high-pressure fresh water, then dry completely. Remove |
| Damaged areas to at least Sa2 1/2 (ISO 8507-1 | 2007) or prepare with power tools to St 3 (ISO 8507-1:2007). |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Optimum results can be achieved even on lightly corroded or damp steel surfaces.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | EPICON T-800 HOLDING PRIMER, EPICON T-800, EPICON T-800 QD, CERABOND 2000 |
|---|---|
| Subsequent coat | EPICON T-800, EPICON T-800 QD |
| Packaging | Two-component |
Note: 1. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
2. Stir the base with an electric stirrer to a uniform state, then thoroughly stir all of the curing agent with the base. Finally add an appropriate amount of thinner and mix thoroughly.
3. Excessive solvent may reduce sag resistance. 4. Mix only the amount of paint that can be used within the specified pot life.
5. *(1) Shade netting is recommended over the coating surface to avoid direct sunlight through manholes or other openings.
If the coating surface has been directly exposed to sunlight, the above “**” indicates the maximum recoat interval
| 6. on steel | Dew point + minimum 5 °C |
|---|---|
| on the film | Dew point + minimum 3 °C. Volume solids, volatile organic content and density are theoretically calculated from a representative formulation without thinner. |
Values vary with formulation for different colours.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.