5988B CMP BIOCLEAN SG-R Modified Epoxy Paint is an epoxy paint. CMP BIOCLEAN SG-R is a two-component anticorrosive coating used in the CMP BIOCLEAN system. Parameters on this page: volume solids 60 ± 2%, dry film thickness 100 µm, theoretical spreading rate 0.167 L/m². Comparable products of the same brand: 5006 ALP 500 Epoxy Paint, 5055 BANNOH 500 Epoxy Paint, 5055D BANNOH 500 AC Epoxy Paint.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "5988B CMP BIOCLEAN SG-R Modified Epoxy Paint"; values such as spreading rate are converted from TDS parameters for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60 ± 2% |
|---|---|
| Dry Film Thickness | 100 µm |
| Theoretical Spreading Rate | 0.167 L/m2 |
| VOC | 385 g/L |
| Density / Specific Gravity | 1.31 g/ml |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 78:22 (by volume) |
| Colour / Appearance | Grey |
CMP BIOCLEAN SG-R is a two-component anticorrosive coating used in the CMP BIOCLEAN system.
| Type | Modified Epoxy Paint |
|---|---|
| Use | Can be used as a primer for the CMP BIOCLEAN antifouling system on propellers and rudders |
| Mixing Ratio | Base : curing agent = 78:22 (by volume) |
|---|---|
| Colour | Grey |
| Flash Point | Base 23.1 °C, curing agent 24.9 °C |
| Density | 1.31 g/ml |
| Volume Solids | 60 ± 2% |
| Volatile organic compound content | 385 g/L |
| Theoretical spreading rate | 0.167 L/m2 |
| Thickness | Wet film 167 µm |
| Dry film | 100 µm |
(dry film = 100 µm)
| Temperature | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 8 h | 7 h | 5.5 h | 4 h | 2.5 h |
| Hard Dry | 36 h | 24 h | 18 h | 10 h | 8 h | |
| Recoat interval | At least | 9 h | 7 h | 6 h | 4 h | 3 h |
At most*
| Pot life | 21 h 18 h 14 h 7 h 4 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 0°C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.6-2 Pa.S |
| Nozzle | Graco621, 623 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | BANNOH 500, EPICON B-100 PRIMER |
| Subsequent coat | CMP BIOCLEAN R |
| Packaging | Two-component |
Note: 1. *Refer to the coating specification.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir the base with a stirrer until uniform, then add the curing agent and mix with the base using a powerful stirrer. Then add an appropriate amount of thinner and mix.
4 Excessive thinner reduces sag resistance.
5 The volatile organic compound content is a theoretical value calculated from the formulation without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.