5409A EPICON MARINE CH Epoxy Paint is an epoxy paint. EPICON MARINE CH is a high-build topcoat based on epoxy polyamide resin, with excellent durability and adhesion. Parameters on this page: volume solids 58 ± 2%, DFT 50-100 µm, theoretical spreading rate 0.086-0.172 L/m2. Comparable products from the same brand: 5006 ALP 500 Epoxy Paint, 5055 BANNOH 500 Epoxy Paint, 5055D BANNOH 500 AC Epoxy Paint.
Parameter source: CMP original Technical Data Sheet (TDS) '5409A EPICON MARINE CH Epoxy Paint'; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 58 ± 2% |
|---|---|
| Dry Film Thickness | 50–100 µm |
| Theoretical Spreading Rate | 0.086-0.172 L/m2 |
| VOC | 422 g/L |
| Density / Specific Gravity | 1.37 g/ml |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 78:22 (by volume) |
| Colour / Appearance | White (standard colour) |
EPICON MARINE CH is a high-build topcoat based on epoxy polyamide resin, with excellent durability and adhesion.
Used as a topcoat for car decks and superstructure interiors.
| Type | Epoxy |
|---|---|
| Use | Used as an anti-corrosive topcoat for car decks (ceilings and walls) and superstructure interiors. |
| Mixing Ratio | Base : curing agent = 78:22 (by volume) |
|---|---|
| Colour | White (standard colour) |
| Flash Point | Base 24°C, curing agent 16°C |
| Density | 1.37 g/ml |
| Volume Solids | 58 ± 2% |
| Volatile organic compound content | 422 g/L |
| Theoretical spreading rate | 0.086-0.172 L/m2 |
| Thickness | WFT 86-172 µm |
| Dry film | 50–100 µm |
(dry film 100 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 4.5 h | 3.5 h | 2 h | 1 h |
| Hard Dry | 45 h | 30 h | 16 h | 12 h | |
| Recoat interval | At least | 28 h | 19 h | 10 h | 8 h |
At most*
| Pot life | 24 h, 12 h, 10 h, 8 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.5Pa.s |
| Nozzle | Graco719, 721 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | CERABOND 2000, EPICON ZINC RICH PRIMER B-2, BANNOH 500, BANNOH 1500BANNOH 2000 and others |
| Subsequent coat | - |
| Packaging | Two-component |
Note: 1 *Refer to the application specification. 2 Due to the nature of EPICON MARINE CH epoxy paint, chalking and fading under UV exposure cannot be avoided.
3 Consult the site technical service representative on colour changes. 4 Density, volume solids and volatile organic content are theoretical calculated values excluding thinner. The values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.