5402E THERMO SHADAN UNDERCOAT EP Epoxy is an epoxy paint. THERMO SHADAN UNDERCOAT EP is a primer based on epoxy polyamide resin, used as the primer for THERMO SHADAN PU. Parameters on this page: volume solids 51 ± 2% (ISO: 3233), dry film thickness 50–100 µm, theoretical spreading rate 0.098–0.196 L/m². Comparable products of the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Data source: CMP original Technical Data Sheet (TDS), "5402E THERMO SHADAN UNDERCOAT EP Epoxy"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 51 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 50–100 µm |
| Theoretical Spreading Rate | 0.098-0.196 L/m2 |
| VOC | 468 g/L (Method 24) |
| Density / Specific Gravity | 1.27 g/ml (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 67:33 (by volume) |
| Colour / Appearance | White |
THERMO SHADAN UNDERCOAT EP is a primer based on epoxy polyamide resin, used as the primer for THERMO SHADAN PU.
| Type | Epoxy |
|---|---|
| Use | As a tie coat for THERMO SHADAN PU, can be used on superstructure exteriors and decks. |
| Mixing Ratio | Base : curing agent = 67:33 (by volume) |
|---|---|
| Colour | White |
| Flash Point | Base 24.0 °C Hardener 27.5 °C |
| Density | 1.27 g/ml (ISO: 2811) |
| Volume Solids | 51 ± 2% (ISO: 3233) |
| Volatile organic compound content | 468 g/L (Method 24) |
| Theoretical spreading rate | 0.098-0.196 L/m2 |
| Thickness | Wet film 98–196 µm |
| Dry film | 50–100 µm |
(dry film 100 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 5.5 h | 4.5 h | 3.5 h | 2.5 h | 1.5 h | 1 h |
| Hard Dry | 55 h | 38 h | 28 h | 16 h | 12 h | ||
| Recoat interval | At least | 55 h | 44 h | 24 h | 18 h | 10 h | 8 h |
At most*
| Pot life | 24 h, 24 h, 24 h, 24 h, 18 h, 12 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.5Pa.s |
| Nozzle | Graco719, 721 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–5% by volume |
| Preceding coat | BANNOH 500, BANNOH 200, BISCON HB NT-L etc. |
| Subsequent coat | THERMO SHADAN PU |
| Packaging | Two-component |
Note: 1. *Refer to the application specification. 2. In confined spaces or at low temperatures, ventilation is necessary to remove the volatilised solvent and promote film formation during application and film formation.
3 Excessive solvent may lead to reduced sag resistance. 4 Application at temperatures down to -5 °C is possible, but reaching hard dry takes a long time, and full cure is only achieved as the temperature rises. 5 Due to the characteristics of epoxy coatings, chalking and fading under UV exposure cannot be avoided.
6 Density, volume solids and VOC content are theoretical calculated values excluding thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.