5073 BANNOH 500 N Epoxy is an epoxy coating. CHUGOKU MARINE PAINTS, LTD BANNOH 500 N is a tar-free epoxy anticorrosive primer based on epoxy resin and pigment. Parameters on this page: volume solids 58 ± 2%, dry film thickness 100 µm, theoretical spreading rate 0.172 L/m². Comparable models from the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Parameter source: CMP original technical data sheet (TDS) for 5073 BANNOH 500 N Epoxy; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 58 ± 2% |
|---|---|
| Dry Film Thickness | 100 µm |
| Theoretical Spreading Rate | 0.172 L/m2 |
| VOC | 405 |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
| Colour / Appearance | Dark purple |
CHUGOKU MARINE PAINTS, LTD BANNOH 500 N is a tar-free epoxy anticorrosive primer based on epoxy resin and pigment. It has excellent physical properties such as a tough, abrasion-resistant film and good adhesion, particularly good adhesion to subsequent antifouling coatings.
| Type | Epoxy |
|---|---|
| Use | Anticorrosive coating for ship bottoms |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
|---|---|
| Colour | Dark purple |
| Flash Point | Base 21 °C Curing agent 23 °C |
| Volume Solids | 58±2% |
| Volatile organic compound content | 405 |
| Theoretical spreading rate | :0.172 L/m2 |
| Thickness | Wet film 172 µm |
| Dry film | 100 µm |
(dry film 100 µm)
| Temperature | -5°C | 0°C | 5°C | 10°C | 20°C | 30°C | |
| Drying Time | Surface Dry | 10 h | 7 h | 5 h | 4 h | 3 h | 2 h |
| Hard Dry | 48 h | 28 h | 18 h | 15 h | 8 h | 6 h | |
| Recoat interval | At least | 48 h | 28 h | 18 h | 15 h | 8 h | 6 h |
At most*
| Pot life | 24 h 24 h 18 h 14 h 7 h 4 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather | Temperature: minimum -5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.6-2.0Pa.s |
| Nozzle | Graco623,621 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | BANNOH 500 |
| Subsequent coat | SEA GRANDPRIX 500, 1000, 2000, CF-10, UNY MARINE, EPICON FINISH HB, etc. |
| Packaging | Two-component |
Note: 1. *Result obtained in consultation with the CMP sales department. 2. In confined spaces or at low temperatures, ventilation is necessary to remove the volatilised solvent and promote film formation during application and film formation.
3. Excessive solvent may reduce sag resistance. 4. Application is possible down to -5 °C, but hard dry takes a long time, and full cure is achieved only as the temperature rises.
5. Volatile organic compound content is a theoretical value calculated without thinner
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.