Product appearance: gloss | Recommended dry film thickness: 1.5 to 3 mm (1 or 3 layers of glass cloth) | Colour: ochre yellow | Recommended wet film thickness: 1.5 to 3 mm | Composition: Two-component | Theoretical spreading rate: actual coverage of 465.60 or 465.61: 2.2 to 5 L/m2; glass cloth: about 0.450 to 1.2 kg/m2 | Drying time: by volume, for 3 mm. Parameters on this page: volume solids 100%, dry film thickness 3000 µm, number of components: Two-component. Comparable products from the same brand: ANTI-MOLD ADDITIVE anti-mould agent, CENTREPOX N EPR, CENTREPOX N.
Parameter source: PPG original technical data sheet (TDS) "ENDOKOTE 465.61"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | — |
|---|---|
| Dry Film Thickness | — |
| Theoretical Spreading Rate | — |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Packaging Specifications | 10 L (Base: 6 L / Curing Agent: 4 L) 20 L (Base: 12 L… |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
Reinforcement with equivalent material.
Property Indoor Outdoor Approved for use in the petroleum industry.*1 Immersion;
Approved for use in nuclear power plants.*2 Strong resistance to aromatic solvents, such as: benzene, toluene, xylene. Shop painting Site painting;
and oxygenated gasoline (MTBE - ETBE). New construction; Maintenance;
Horizontal surfaces: use ENDOKOTE 465.60(1) Vertical surfaces and topcoat: use ENDOKOTE 465.61 Suitable environment:
*1 French Military Fuel Department (N0.78 DC-SEA/2), CNPC Engineering Research Institute; suitable for long-term contact with petroleum fuels, oxygenated gasoline (MTBE – *2 Électricité de France, nuclear laboratory, nuclear energy centre ETBE), water and others (please consult our Technical Service Department, Beijing Nuclear Engineering Institute gate).
Product Appearance Recommended DFT Gloss 1.5–3 mm (1 or 3 layers of glass cloth) Colour Recommended WFT Ochre yellow 1.5–3 mm Component Theoretical Spreading Rate Two-component Actual coverage: 465.60 or 465.61: 2.2–5 L/m² glass Mixing Ratio cloth: approx. 0.450–1.2 kg/m² Drying Time By volume For 3 mm:
Base: 60% Dust-free: 15 h Curing agent: 40% Touch dry: 24 h Usable: 7 days Thinner (impregnation) No thinning required Maturation period Recoatable No activation period 30 min itself * Ambient temperature affects the activation period and minimum recoating interval Density Recoating interval 1.15 ± 0.05 For 3 mm:
Solids content Minimum*: none (topcoat: 24 h) – Maximum*: 5 days Temperature resistance By volume*: 100% Immersible in petroleum fuel at 95 °C. For higher temperatures, consult our Technical Department.
| All data relating to the density | and solids content of the topcoat are based on the product being white. These data are also based on proper mixing of the product. |
|---|
*See Overview.
J 02/03 Vertical surfaces: pre-treat the seams and rivet lines of riveted tanks with ENDOKOTE 465.11 first; ENDOKOTE 481.40 is preferred.
If necessary, mix ENDOKOTE 481.40 or ENDOKOTE 465.11 with quartz sand to form a mastic for filling surface seams or pores.
| Roll-apply Enduk with a roller | 465.61, then incorporate pre-cut glass cloth. |
|---|---|
| Then roll-apply Enduk with a roller | 465.61, ensuring complete penetration of the glass cloth. |
Carefully squeeze out residual air bubbles with a special plastic roller.
Repeat the operation once (2 layers of glass cloth) or twice (3 layers of glass cloth) as specified in the technical requirements.
After 24 h at 20 °C ambient temperature, apply topcoat ENDOKOTE 465.61 by roller or spray ENDOKOTE 465.11 with a conventional high-pressure spray gun.
Recommended average thickness: 1.5 mm (1 layer of glass cloth) / 2–2.5 mm (2 layers of glass cloth) / 3 mm (3 layers of glass cloth). Pre-treat welds, rivets and hard-to-reach areas on horizontal surfaces with ENDOKOTE 465.11 first.
If necessary, use ENDOKOTE 481.40, ENDOKOTE 465.10 or ENDOKOTE 465.11, or mix ENDOKOTE 465.60/61 with quartz sand as a mastic to fill surface seams or pores.
| Roll-apply Enduk with a roller | 465.60, then incorporate pre-cut glass cloth. |
|---|---|
| Then roll-apply Enduk with a roller | 465.60, ensuring complete penetration of the glass cloth. |
Repeat the operation once (2 layers of glass cloth) or twice (3 layers of glass cloth) according to the technical requirements.
After 24 h at 20 °C ambient temperature, apply topcoat ENDOKOTE 465.61 by roller.
Recommended average thickness: 1.5 mm (1 layer of glass cloth) / 2–2.5 mm (2 layers of glass cloth) / 3 mm (3 layers of glass cloth) SigmaKalon Coatings (China) Room 408, Baiteng Building, 318 Fuzhou Road, Shanghai – Postcode: 200001 Tel: 021-6391-2991 Fax: 021-6391-2700 J 02/J 03 Application Instructions Substrate and Surface Preparation Substrate type: suitable primer or sealer, required to be clean, dry and repaired.
| On the primed surface: | Sigmacover PZ sealer surface: Fidapox 240 Use/thinning Product preparation: |
|---|
Stir the base mechanically and slowly add the curing agent until thoroughly mixed.
Tool Thinner Nozzle pressure
| Brush | Not available | None |
| Roller / special roller | Suitable | None |
| Air spray gun | Not available | None |
| High-pressure spray gun | Not available | None |
Application conditions:
Ambient temperature: +5 °C to +35 °C Substrate temperature: at least +3 °C above dew point Note: minimum application temperature is 10 °C.
For better results, it is recommended that the product temperature during application be above 20 °C; preheat if necessary.
| (1) | Where the slope exceeds 4%, use ENDOKOTE 465.61. |
|---|
Health and safety; flash point:
Base and hardener: flash point >55 °C. Thinner No. 22: 21 °C < flash point < 55 °C. Volatile organic content per litre: 0 g/L. This value complies with the European paint and varnish sample criteria.
Packaging and storage
| Packaging: | 10 L (base: 6 L / curing agent: 4 L) 20 L (base: 12 L / curing agent: 8 L) Storage: unopened indoors between +5 °C and +35 °C, shelf life at least 12 months. |
|---|
SigmaKalon Coatings (China) Room 408, Baiteng Building, 318 Fuzhou Road, Shanghai – Postcode: 200001 Tel: 021-6391-2991 Fax: 021-6391-2700 J 02/J03
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.