Seablue-A/F783 Self-Polishing Antifouling Paint is an antifouling paint. Parameters on this page: volume solids approx. 58% (determined per ISO 3233), DFT 100–150 µm (single coat), theoretical spreading rate 5.75 m²/L/100 µm. Comparable models from the same brand: EgisPacific Self-Polishing Antifouling Paint, Seablue-A/F783 Self-Polishing Antifouling Paint.
Parameter source: KCC original technical data sheet (TDS) "Seablue-A/F783 Self-Polishing Antifouling Paint"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 58% |
|---|---|
| Dry Film Thickness | 100–150 µm (single coat) |
| Theoretical Spreading Rate | 5.75 m²/L/100 µm |
| VOC | — |
| Density / Specific Gravity | 1.6–1.9 kg/L (mixture, depending on colour) |
| Number of Components | One-component |
| Flash Point | 26 °C (closed) |
| Thinner | No. 002 (by volume) |
| Colour / Appearance | Flat, reddish-brown, dark brown |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Seablue A/F783 is a tin-free high-performance pure self-polishing antifouling paint, ensuring maximum antifouling effect against a wide range of marine flora and fauna for all types of ocean-going and offshore vessels, with no pollution of the marine environment. Seablue A/F783 complies with the IMO Anti-fouling Systems Convention (AFS/CONF/26).
Environmentally friendly antifouling paint for newbuildings or repaired vessels requiring long-term protection in harsh environments or operating in areas where organotin antifouling paints are restricted.
| Appearance and colour | Flat, reddish-brown, dark brown |
|---|---|
| density | Mixture, depending on colour, approx. 1.6–1.9 |
| Volume Solids | Seablue A/F783: approx. 58% (determined per ISO 3233); A/F783(H), A/F783(L): approx. 52% |
| Theoretical Spreading Rate | At 125 µm DFT on a smooth surface: A/F783 4.6 m²/L; A/F783(H), A/F783(L) 4.2 m²/L |
| Flash Point | 26 °C (closed) |
Completely remove rust, dust, moisture, oil and other contaminants from the substrate surface with fresh water or a suitable solvent.
Korabor Aluminum H.B RH248, Kovinyl Sealer VH137AL, Korepox H.B EH2560 Korepotar H.B. EH173(S)
Brush, roller, spray (conventional spray or airless spray). Airless spray: nozzle tip size 635–787 µm (0.025"–0.031"); spray pressure 20.7–27.1 MPa. * Clean application tools immediately after use with Thinner No.002.
Thinner No. 002 (by volume).
* The surface shall be clean and dry; ambient temperature during application and curing shall be 10–40°C. Relative humidity shall be below 85%. * Substrate surface temperature shall be at least 3°C above dew point. * In winter, apply where substrate and air temperature are above 10°C, and maintain the curing temperature above 5°C after application.
Dry film thickness per coat 100–150 µm; apply 2–3 coats according to the number of coats specified. Film thickness may be adjusted according to area and service.
| Substrate temperature | 5°C | 20°C | 30°C |
|---|---|---|---|
| Touch dry | 8 h | 2 h | |
| Curing/drying | 18 h | 6 h | 4 h |
At 20°C, minimum 6 h, maximum unlimited. If the maximum recoating interval is exceeded, surface roughening is required.
| Shelf life | 12 months |
|---|---|
| Packaging Specifications | 18 L packaging |
* Protect skin and eyes; avoid prolonged inhalation of solvent vapour. * Ensure adequate ventilation; respiratory protective equipment must be worn when working in confined spaces. * Avoid moisture and direct light during storage. Issue date: 2010-06-01.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.