KOREPOX TOP COAT ET5641 Epoxy Topcoat is an epoxy coating used as a topcoat. Parameters on this page: volume solids approx. 34–40%, dry film thickness 20–30 µm, theoretical spreading rate 3.2 m²/L/100 µm. Comparable products of the same brand and type: KOREPOX TOP COAT ET5641 Epoxy Topcoat, KOREPOX TOP COAT H.B. ET5740 Epoxy Topcoat, Korepox Topcoat H.B. ET5745 Epoxy Topcoat.
Parameter source: KCC original technical data sheet (TDS) "KOREPOX TOP COAT ET5641 Epoxy Topcoat"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 34–40% |
|---|---|
| Dry Film Thickness | 20–30 µm |
| Theoretical Spreading Rate | 3.2 m²/L/100 µm |
| VOC | — |
| Density / Specific Gravity | 1.1–1.2 kg/L |
| Number of Components | One-component |
| Flash Point | 23–32 °C (closed) |
| Colour / Appearance | Matte, semi-gloss. Black |
| Packaging Specifications | 18 L packaging |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
KOREPOX TOP COAT ET5641 is a baking-type enamel based on epoxy resin, featuring excellent film strength, corrosion resistance, durability, chemical resistance, water resistance, abrasion resistance and rust prevention; solvent resistance and impact resistance are also excellent, and resistance to synthetic detergents is excellent. ET5641 is a heavy-metal-free product and provides excellent anti-corrosion performance with a single coat.
Anti-rust paint for automotive parts and other iron materials.
| Appearance and colour | Matte, semi-gloss. Black. |
|---|---|
| density | 1.1~1.2 (Kg/L) |
| Volume Solids | Approx. 34–40% |
| Theoretical Spreading Rate | Dry film thickness 25 µm on a flat surface, approx. 12.8 m²/L |
| Flash Point | 23–32 °C (sealed) |
| Viscosity | 65~75KU |
* Remove rust, dust, oil and other contaminants from the substrate by appropriate methods (blast cleaning Sa 2½ or zinc phosphate film). * For repair coating, sand the defective areas and dry completely.
Air spray: nozzle orifice 1.3–1.5 mm; spray pressure 4–5 kg/cm²; number of coats 2–3 (passes). * Coating defects may occur with brush, roller, airless spray, electrostatic and dip coating; consult the research department.
024, 088(MD), 088(KD). * Dilution viscosity: 18–22 s (20 °C) / Ford Cup No. 4 (for air spray). * Dilution ratio: 20–30% (by volume). * Do not dilute components separately; the mixture must be diluted. * The specified thinner must be used.
To prevent condensation, the substrate temperature must be at least 3 °C above the dew point; the ideal substrate temperature during application is 15–25 °C with a relative humidity of 35–80%. The surface must be clean and dry; avoid humid weather.
Dry film thickness 20–30 µm.
120 °C × 25–35 min (substrate surface temperature). 150 °C × 20–25 min (substrate surface temperature). (Failure to observe the baking temperature may reduce properties such as corrosion resistance and impact resistance.)
| Shelf life | 12 months |
|---|---|
| Storage | May deteriorate over time; avoid direct light and ignition sources; store at ambient temperature (5–35 °C) in a well-ventilated, dry, cool and dark room, and use within the shelf life. |
| Packaging Specifications | 18 L packaging |
1. Wear respiratory protective equipment when applying in enclosed spaces. 2. Sedimentation may occur during storage; stir thoroughly before use. 3. Seal and store any remaining material after use. 4. Keep away from ignition sources and ensure adequate ventilation. 5. Avoid skin and eye contact; do not inhale solvent vapour for prolonged periods. 6. In case of eye contact, rinse with water for approx. 15 min, then immediately seek treatment from a specialist at a hospital. Issue date: 2012-08-01.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.