Jota AY30T Quick-drying Acrylic Primer/Topcoat 30T belongs to acrylic paints and is used as a topcoat. Industrial protective coatings segment: recommended for new-build and maintenance industrial buildings and a range of equipment, including but not limited to engines, machinery, vehicle bodies and special-purpose vehicles. This is a one-component physically drying acrylic coating. Parameters on this page: volume solids 57 ± 2%, DFT 60–110 µm, theoretical spreading rate 9.5–5.2 m²/L. Comparable models from the same brand: Conseal Touch-Up one-component physically drying acrylic coating, Hardtop CA two-component acrylic topcoat, Hardtop One moisture-curing acrylic polysiloxane topcoat.
Parameter source: JOTUN original technical data sheet (TDS) "Jota AY30T Quick-drying Acrylic Primer/Topcoat 30T"; values such as spreading rate are converted from TDS parameters and serve as selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 57 ± 2% |
|---|---|
| Dry Film Thickness | 60–110 µm |
| Theoretical Spreading Rate | 9.5–5.2 m²/L |
| VOC | 414 g/L (China) |
| Density / Specific Gravity | 1.5 kg/L |
| Number of Components | One-component |
| Flash Point | 25 °C |
| Thinner | Jotun Thinner No. 16 |
| Gloss | Semi-gloss (35–70) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Jota AY30T
This is a one-component physically drying acrylic coating. Its film is semi-gloss with good gloss retention. It is a high-build product. It dries quickly. It can be applied directly to metal. It is used as a topcoat in atmospheric environments. It can be applied at surface temperatures below 0°C.
Industrial protective coatings:
Recommended for new construction and maintenance of industrial plants and a range of equipment, including engines, machinery, carriages and special vehicles.
Suitable as a topcoat forming part of a complete coating system, for the protection and decorative colour finishing of concrete.
Others
Tinted according to the colour chart and using the industrial tinting system (MCI)
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 57± 2 % |
| Gloss (GU 60°) | ISO 2813 | Semi-gloss (35–70) |
| Flash Point | ISO 3679 Method 1 | 25 °C |
| Density | Theoretical Value | 1.5 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| China | Mandatory national standard of China | GB 30981.2-2025 | 414 g/L |
| Coating hazards GB | 30981.2-S-Pb≤1000-NC |
The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 60–110 µm |
| Wet Film Thickness | 105–190 µm |
| Theoretical Spreading Rate | 9.5–5.2 m²/L |
Bright colours may require a higher dry film thickness within the recommended range to achieve hiding.
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | St 2 (ISO 8501-1) | Sa 2½ (ISO 8501-1) |
| Aluminium | The surface should be blasted with a non-metallic abrasive, | “Blast clean using an approved non-metallic abrasive |
| hand- or machine-sanded using abrasive paper or fibre discs, | to produce a sharp angular surface profile.” |
to produce scratch marks on the surface.
Coated surfaces: clean, dry and intact compatible primer. Sa2½ (ISO 8501-2).
This product may be applied by the following methods
| Spray: | Apply by airless spray. (10% thinning) |
| Brush: | Use a suitable brush. Take care to achieve the specified dry film thickness. |
| Roller: | May be used, but not recommended as a first coat on bare steel. Care shall be taken to achieve the specified film thickness. |
One-component
| Thinner: | Jotun Thinner No. 7 | /Jotun Thinner No. 16 |
| JOTUN Thinner No. 7 | JOTUN Thinner No. 16 |
| Nozzle tip size (inch/1000): | 15-21 |
| Nozzle pressure (minimum): | 150 bar / 2100 psi |
| Substrate Temperature | -10 °C | -5 °C | 0 °C | 5 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 60 min | 50 min | 35 min | 25 min | 20 min | 15 min | 10 min |
| Handle dry | 16 h | 12 h | 10 h | 8 h | 5 h | 4 h | |
| Minimum recoat interval | 3 h | 2 h | 1 h | ||||
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
Drying time data at -10 °C were measured at a DFT of 60 µm.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Handle dry | The minimum time after application before handling will not damage the film. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 60 °C | |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy, modified epoxy, acrylic |
| Subsequent coat: | Acrylic |
| Volume | Container Size | |
| (L) | ||
| Jota AY30T Fast-drying Acrylic Primer/Topcoat 30T | 5 / 20 | |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
Jota AY30T 12 months Quick-drying Acrylic Primer/Topcoat 30T
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.