Hardtop Pro Acrylic Polysiloxane Topcoat is an acrylic paint, used as a topcoat. Industrial protective coatings: recommended for marine engineering, oil depots, refineries, power plants, bridges and buildings. This product contains no isocyanates and does not produce diisocyanates during hot work/welding or fire accidents. Parameters on this page: volume solids 65 ± 2%, dry film thickness 50–130 µm, theoretical spreading rate 13–5 m²/L. Comparable products of the same brand: Conseal Touch-Up Single-component Physically Drying Acrylic, Hardtop CA Two-component Acrylic Topcoat, Hardtop One Moisture-curing Acrylic Polysiloxane Topcoat.
Data source: JOTUN original Technical Data Sheet (TDS), "Hardtop Pro Acrylic Polysiloxane Topcoat"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 65 ± 2% |
|---|---|
| Dry Film Thickness | 50–130 µm |
| Theoretical Spreading Rate | 13–5 m²/L |
| VOC | 322 g/L (China) |
| Density / Specific Gravity | 1.4 kg/L |
| Number of Components | Two-component |
| Flash Point | 28 °C |
| Thinner | Jotun Thinner No. 2 / Jotun Thinner No. 26 |
| Mixing Ratio | 3 parts : 1 part (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Hardtop Pro
This is a two-component chemically cured acrylic-modified polysiloxane coating. It is a high-solids product. Its film surface has high gloss. Excellent gloss and colour retention. It has excellent mechanical properties and chemical resistance. Used as a topcoat in atmospheric environments. This product can be recoated at any stage of curing. It can cure at temperatures as low as 0 °C. This product contains no isocyanates and does not produce diisocyanates during hot work/welding or fire accidents.
Industrial protective coatings:
Recommended for marine engineering, oil depots, refineries, power plants, bridges and buildings. Widely suitable for industrial buildings.
Marine coatings:
Recommended for freeboard, decks and superstructures.
Others
Pre-qualified in the selected coating system in accordance with NORSOK M-501; certified compliant with the low flame-spread requirements of the IMO 2010 FTP Code. For details, consult your JOTUN representative.
Other certificates and approvals are available on request.
Tinted according to the colour card and using the industrial tinting system (MCI). Some warning colours
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 65± 2 % |
| Gloss (GU 60°) | ISO 2813 | Gloss (70–85) |
| Flash Point | ISO 3679 Method 1 | 28 °C |
| Density | Theoretical Value | 1.4 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 297 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | Calculation | 297 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 297 g/L |
| China | Mandatory national standard of China | GB 30981.2-2025 | 322 g/L |
Coating hazards GB 30981.2-S-Pb≤1000-NC. The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 50–130 µm |
| Wet Film Thickness | 75–200 µm |
| Theoretical Spreading Rate | 13–5 m²/L |
Bright colours may require a higher dry film thickness within the recommended range to achieve hiding.
Surface Preparation
| Substrate | Minimum | Recommended |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Spray: | Apply by air spray or airless spray. |
| Brush: | Use a suitable brush. Take care to achieve the specified dry film thickness. |
| Roller: | Use a suitable roller. Take care to achieve the specified dry film thickness. |
| Hardtop Pro Comp A — Acrylic Polysiloxane Topcoat, Component A | 3 parts |
| Hardtop Pro Comp B Acrylic Polysiloxane Topcoat, Component B | 1 part |
| Thinner: | Jotun Thinner No. 10 | / Jotun Thinner No. 2 / Jotun Thinner No. 26 |
| JOTUN Thinner No. 10 | JOTUN Thinner No. 26 |
When a xylene-free solvent is required, Jotun Thinner No. 2 can be used.
Due to local legislation, Jotun Thinner No. 26 is supplied and used in the United States.
When applying this product on in-service structures, consult the local Jotun representative.
The amount of thinner added must not exceed local health, safety and environmental regulations.
| Nozzle tip size (inch/1000): | 13-19 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
| Substrate Temperature | 0 °C | 5 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 15 h | 10 h | 7 h | 5 h | 3 h |
| Walk-on Dry | 32 h | 25 h | 20 h | 8 h | 4 h |
| Minimum recoat interval | 32 h | 25 h | 20 h | 8 h | 4 h |
| Dry/cured to service | 20 days | 15 days | 10 days | 5 days | 3 days |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Induction Time | 15 min |
| Pot Life | 3 h |
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 120°C | 140 °C |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy, modified epoxy, polyurethane, polysiloxane, two-component acrylic |
| Subsequent coat: | Polysiloxane |
| Volume | Container Size | |
| (L) | ||
| Hardtop Pro Comp A — Acrylic Polysiloxane Topcoat, Component A | 3.75/15 | 5/20 |
| Hardtop Pro Comp B Acrylic Polysiloxane Topcoat, Component B | 1.25/5 | 3/5 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| Hardtop Pro Comp A — Acrylic Polysiloxane Topcoat, Component A | 24 months |
| Hardtop Pro Comp B Acrylic Polysiloxane Topcoat, Component B | 12 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
This product can contribute to green building standard credits. Visit Jotun.com for more information or contact your local JOTUN representative.
EPDs are available at www.epd-norge.no
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.