8052 CERABEST Grey is a heat-resistant paint belonging to the heat-resistant coatings category. CERABEST is a coating formed by combining selected heat-resistant alloys with silicate solutions. It has excellent heat resistance, withstanding temperatures up to 800 °C. It also has good adhesion to inorganic zinc primers. Parameters on this page: volume solids 42 ± 2%, dry film thickness 30 µm, theoretical spreading rate 0.071 L/m². Comparable products from the same brand: 8033 SILICON HR silicone resin heat-resistant paint, 8033B SILICON HR BLACK silicone resin heat-resistant paint, 8034 SILICON HR SILVER silicone heat-resistant aluminium paint.
Parameter source: CMP original technical data sheet (TDS) for 8052 CERABEST Grey; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 42 ± 2% |
|---|---|
| Dry Film Thickness | 30 µm |
| Theoretical Spreading Rate | 0.071 L/m2 |
| VOC | 554 g/L |
| Density / Specific Gravity | 1.51 g/mL |
| Number of Components | Two-component |
| Thinner | INORGANIC SHOP THINNER Series (depending on actual… |
| Mixing Ratio | Slurry : base = 44:56 (by volume) |
| Colour / Appearance | Grey |
CERABEST is a coating formed by combining selected heat-resistant alloys with silicate solutions.
It has excellent heat resistance, withstanding temperatures up to 800 °C. It also has good adhesion to inorganic zinc primers.
| Type | Super Heat-resistant Paint |
|---|---|
| Use | Can be applied over inorganic shop primer to provide thermal protection for steel structures (such as ship superstructures). |
| Mixing Ratio | Slurry : base = 44:56 (by volume) |
|---|---|
| Colour | Grey |
| Flash Point | Paste 13.6 °C, Base 13 °C |
| Density | 1.51 g/mL |
| Volume Solids | 42±2% |
| Volatile organic compound content | 554 g/L |
| Theoretical spreading rate | 0.071 L/m2 |
| Dry Film Thickness | 30 µm |
| (dry film 30 µm) | Temperature | 5 °C | 10 °C | 20 °C | 30 °C |
| Drying time, touch dry | 12 min | 8 min | 4 min | 2 min | |
| Hard Dry | 60 h | 48 h | 30 h | 15 h | |
| Recoat interval | At least organic system | 14 days | 10 days | 7 days | |
| At most | 180 days | 180 days | |||
| Pot life | 30 h | 24 h | 16 h | 10 h |
| Application method | Airless spray, conventional spray |
|---|---|
| Weather: temperature | 5-35°C |
| Humidity | 50–90% RH; steel temperature at least 3 °C above dew point |
| Airless spray: viscosity | 9–10 s (Iwata cup #4) |
| Nozzle | Graco 619,719 |
| Paint output pressure | 8.8-11.8 Mpa |
| Spray gun speed | 30–50 cm/s |
| Thinner | INORGANIC SHOP THINNER Series (depending on actual conditions) |
| Thinning | 0–7% by volume |
| Preceding coat | Inorganic shop primer |
| Subsequent coat | Epoxy resin paint, epoxy-bitumen paint, tar-free epoxy paint, chlorinated rubber primer, alkyd primer |
| Packaging | Two-component |
Note: 1 For light grey and white, there is a separate product data sheet; the mixing ratio is different.
2 Do not use "BASE A". "BASE A" is only for light grey and white. "CERABEST Grey BASE" and "CERABEST BASE" are the same product.
3 Stir the paste thoroughly first, then mix with the base to obtain a uniform mixture;
4 Use an 80-mesh filter at the pump inlet to prevent nozzle clogging;
5 Keep the paint agitated during application to prevent pigment settling;
6 In high-humidity environments, use the mixed paint as soon as possible to avoid reaction of the paint mixture with moisture;
7 Use the specified thinner;
8 Since curing is relatively slow at low temperatures, below 10 °C the overcoating interval with the subsequent coat is 7 days;
9 Select the thinner type according to weather conditions:
| Inorganic shop thinner QD | Below 10 °C |
|---|---|
| Inorganic shop thinner A | Below 10 °C |
| Inorganic shop thinner S | 25-30°C |
| Inorganic shop thinner SS | Above 30 °C, if the application area is exposed to direct sunlight, select based on steel surface temperature. |
10 Density and volatile organic compound content are theoretical calculated values excluding thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.