6195 UMEGUARD SUPER-H PRIMER Epoxy Paint is an epoxy coating used as a primer. UMEGUARD SUPER-H PRIMER is the epoxy primer specially matched to UMEGUARD SUPER-H, with high roughness, abrasion resistance and adhesion, and high anticorrosive performance in dry cargo holds handling coal and iron. Parameters on this page: volume solids 63 ± 2%; dry film thickness 100–200 µm; theoretical spreading rate 0.16–0.32 L/m². Comparable products from the same brand: 1050 NZ PRIMER S Zinc-free Epoxy Shop Primer, 200 GALVANITE No.200 PRIMER Epoxy Galvanized Steel Primer, 400 GALVANITE No.400 PRIMER Epoxy Polyamide Primer.
Source: CMP original technical data sheet (TDS) '6195 UMEGUARD SUPER-H PRIMER Epoxy Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 63 ± 2% |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.16-0.32 L/m2 |
| VOC | 401 g/L |
| Density / Specific Gravity | 1.31 g/mL |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
| Colour / Appearance | Grey, red-brown |
UMEGUARD SUPER-H PRIMER is the epoxy primer specially matched to UMEGUARD SUPER-H, with high roughness, abrasion resistance and adhesion, and high anticorrosive performance in dry cargo holds handling coal and iron.
It is suitable as a protective primer for cargo holds.
| Type | Epoxy |
|---|---|
| Use | May be used as an anticorrosive coating for the cargo holds of bulk carriers. |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
|---|---|
| Colour | Grey, red-brown |
| Flash Point | Base 23.1 °C, curing agent 24.9 °C |
| Density | 1.31 g/mL |
| Volume Solids | 63 ± 2% |
| Volatile organic compound content | 401 g/L |
| Theoretical spreading rate | 0.16-0.32 L/m2 |
| Thickness | WFT 159–317 µm, DFT 100–200 µm |
(dry film 200 µm)
| Temperature | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 5.5 h | 4 h | 2.5 h |
| Hard Dry | 18 h | 10 h | 8 h | |
| Recoat interval | At least | 18 h | 10 h | 8 h |
| At most | 10 days | 10 days | ||
| Pot life | 14 h | 7 h | 4 h | |
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 10 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.6-2.0 Pa.s |
| Nozzle | (Graco)623,621 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | CERABOND and others |
| Subsequent coat | UMEGUARD SUPER-H |
| Packaging | Two-component |
Note: 1. *Consult the CMP sales department.
2. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
3. Volume solids and VOC content are theoretical calculated values based on the formulation without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.