400 GALVANITE No.400 PRIMER Epoxy Polyamide Resin Primer is an epoxy coating used as a primer. GALVANITE No.400 PRIMER is a primer for galvanised steel based on epoxy resin and polyamide resin with special anticorrosive pigments. Parameters on this page: volume solids 47 ± 2% (ISO 3233), dry film thickness 30-50 µm, theoretical spreading rate 0.064-0.106. Comparable models from the same brand: 1050 NZ PRIMER S zinc-free epoxy shop primer, 200 GALVANITE No. 200 PRIMER epoxy galvanised steel primer, 5106D EPICON PRIMER HB epoxy primer.
Parameter source: CMP original technical data sheet (TDS) for 400 GALVANITE No.400 PRIMER Epoxy Polyamide Resin Primer; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 47 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 30–50 µm |
| Theoretical Spreading Rate | — |
| VOC | 482 g/L (Method 24) |
| Density / Specific Gravity | 1.38 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 69:31 (by volume) |
| Colour / Appearance | White |
GALVANITE No.400 PRIMER is a primer for galvanised steel based on epoxy resin and polyamide resin with special anticorrosive pigments.
| It has the following advantages | 1. Excellent adhesion to galvanised surfaces 2. Excellent application properties 3. Good compatibility with various coatings 4. Excellent oil and chemical resistance |
|---|
| Type | Epoxy polyamide resin primer |
|---|---|
| Use | May be used as a primer for galvanized steel |
| Mixing Ratio | Base : curing agent = 69:31 (by volume) |
|---|---|
| Colour | White |
| Flash Point | Base 17.5 °C; curing agent 26.3 °C |
| Density | 1.38 g/mL (ISO: 2811) |
| Volume Solids | 47 ± 2% (ISO: 3233) |
| Volatile organic compound content | 482 g/L (Method 24) |
| Theoretical spreading rate | 0.064-0.106 |
| Wet Film Thickness | 64–106 µm |
| Dry Film Thickness | 30–50 µm |
(dry film 40 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3.5 h | 2.5 h | 1.5 h | 1 h |
| Hard Dry | 34 h | 24 h | 14 h | 10 h | |
| Recoat interval | At least | 34 h | 24 h | 14 h | 10 h |
| At most | 14 days | 14 days | |||
| Pot life | 34 h | 24 h | 14 h | 10 h | |
| Induction Time | 30 min | 15 min | - |
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% |
| Airless spray: viscosity | 55–65 s (Ford Cup #4) |
| Nozzle | Graco 619,719 |
| Paint output pressure | 10.8-13.7 Mpa |
| Spray gun speed | 80–100 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | - |
| Subsequent coat | EPICON series, UNYMARINE |
| Packaging | Two-component |
Note: 1. Application is possible when the temperature drops to -5 °C, but hard drying takes a long time, and full cure is only achieved as the temperature rises.
2. Density, volume solids and VOC content are theoretical calculated values without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.