5916 SEA GRANDPRIX FBX KAI WHITE Tin-free Self-polishing Antifouling is an antifouling. SEA GRANDPRIX FBX KAI WHITE is a tin-free self-polishing antifouling based on a special resin with high hydrolysis activity. Parameters on this page: volume solids 45 ± 2% (by volume), dry film thickness 50–100 µm, theoretical spreading rate 0.111–0.222 L/m². Comparable products from the same brand: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling.
Source: CMP original technical data sheet (TDS) "5916 SEA GRANDPRIX FBX KAI WHITE Tin-free Self-polishing Antifouling"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 45 ± 2% (by volume) |
|---|---|
| Dry Film Thickness | 50–100 µm |
| Theoretical Spreading Rate | 0.111-0.222 L/m2 |
| VOC | 562 g/L |
| Density / Specific Gravity | 1.30g/ml |
| Number of Components | One-component |
| Flash Point | 25.0°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | White |
SEA GRANDPRIX FBX KAI WHITE is a tin-free self-polishing antifouling based on a special resin with high hydrolysis activity.
Good antifouling performance derives from the highly active polymer, which ensures high efficacy and release of the biocide.
Provides long-term antifouling protection through a controlled hydrolysis maintaining surface activity.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | Can be used as an antifouling for the waterline area of ocean-going steel vessels to extend dry-docking intervals. |
| Colour | White |
|---|---|
| Flash Point | 25.0°C |
| Density | 1.30g/ml |
| Volume Solids | 45 ± 2% (by volume) |
| Volatile organic compound content | 562 g/L |
| Theoretical spreading rate | 0.111-0.222 L/m2 |
| Thickness | Wet film 111–222 µm, dry film 50–100 µm |
(dry film 100 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 12 h | 8 h | 5 h | 4 h | |
| Recoat interval | At least | 12 h | 8 h | 5 h | 4 h |
At most *
| Dry-to-launch time | Fastest 24 h 18 h 12 h 10 h |
|---|
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 60 s (Ford No. 4 cup) |
| Nozzle | (Graco)621-723 |
| Paint output pressure | 11.7-14.7MPa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Preceding coat | SILVAX SQ-K, RAVAX AC-HB, among others |
Subsequent coat:
| Packaging | One-component |
|---|
Note: 1. If a ship berths continuously for two weeks or longer, especially in areas at risk of heavy marine growth, the bottom antifouling areas may be fouled by marine organisms.
2. Density, volume solids and VOC are theoretical calculated values excluding thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.