Chlorinated Rubber Primer XH4301 belongs to chlorinated rubber coatings and is used as a primer. It can be applied to steel structure surfaces under moderate to severe corrosive environments (including seawater immersion areas). Parameters on this page: volume solids 45 ± 2%, dry film thickness 60/80/100 µm, theoretical spreading rate 4.3 m²/L.
Parameter source: T&H manufacturer's Technical Data Sheet (TDS) "Chlorinated Rubber Primer XH4301"; spreading rate and other values are converted from the TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 45 ± 2% |
|---|---|
| Dry Film Thickness | 60/80/100 µm |
| Theoretical Spreading Rate | 4.3 m2/L |
| VOC | 510g/L |
| Density / Specific Gravity | 1.3 kg/L |
| Number of Components | One-component |
| Flash Point | 25°C |
| Thinner | 5-15% |
| Colour / Appearance | A limited range of colours such as grey and iron red |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Curing agent: none
A primer based on chlorinated rubber. It can be applied to steel structure surfaces under moderate to severe corrosive environments (including seawater immersion areas).
| Colour | A limited range of colours such as grey and iron red |
|---|---|
| Gloss | N/A |
| density | 1.3 kg/L |
| Volume Solids | 45±2% |
| Volatile Organic Compounds | 510g/L |
| Flash Point | 25°C |
| Typical dry film thickness | 80µm |
|---|---|
| Recommended dry film thickness | 60–100 µm, depending on system requirements |
| Thinner quantity (by volume) | Airless spray 5–15% | Air spray 10–30% | Roller or brush 5–15% |
| Recommended nozzle size | 0.43~0.64mm | 1.5~2.5mm | / |
| Recommended spray pressure | 15~20MPa | 0.3~0.6MPa | / |
| Application suitability | Recommended | ||
| Dry film thickness (µm) | 60 | 80 | 100 |
| Wet film thickness (µm) | 133 | 177 | 222 |
| Theoretical spreading rate (m²/L) | 7.2 | 5.4 | 4.3 |
| Temperature | Surface Dry | Hard Dry | Pot Life | Recoat interval | |
| Minimum | Maximum* | ||||
| 5°C | 4h | 16h | / | 24h | / |
| 15°C | 2h | 8h | / | 8h | / |
| 25°C | 1h | 4h | / | 6h | / |
| 40°C | 1h | 4h | / | 6h | / |
*The maximum recoat interval depends on the exposure environment and the end use of the coating.
All surfaces to be coated shall be clean, dry and free from contamination. Before application, all surfaces shall be assessed and prepared in accordance with ISO 8504:2000. Blast clean to Sa2½ (ISO 8501-1:2007). If oxidation occurs between blasting and application of this product, the surface shall be re-blasted to the specified visual standard. Surface defects exposed by blasting shall be abraded, filled or otherwise treated. The product is suitable for application over surfaces blast-cleaned to the above standard and then, under good shop
conditions, naturally aged for no more than 7 to 10 days. Where the coating film has suffered mechanical damage with localised rusting, it shall be abraded, filled or otherwise treated. The surface quality may be reduced to Sa2, but loose powdery deposits shall not be present.
1. During application, ensure ventilation and exhaust, keep away from sources of ignition, and wear protective equipment such as a mask and gloves; maintain adequate ventilation also during curing. 2. Adjust the thinner quantity according to temperature, mix thoroughly, and filter through a 120-mesh copper screen before use. Seal unused paint if not used for a long time, otherwise skinning occurs; if skinning occurs, remove the skin before use. 3. The film thickness may be adjusted according to the intended use and area. This will alter the spreading rate, drying time and recoat interval. The normal dry film thickness range is 60–100 µm. Repeated maintenance may make the total film too thick, causing blistering. As each coat may retain solvent, avoid applying this product too thickly. 4. As this product is thermoplastic, prolonged mechanical load above about 40 °C will indent the film. Once the temperature falls, the mechanical strength of the film recovers. 5. During application and curing, the substrate temperature must be above 5 °C and at least 3 °C above the dew point, with relative humidity not more than 85%. Temperature and relative humidity must be measured on the substrate near the work area. 6. Cutting of structures coated with this product produces fume; take appropriate protection. 7. When work is interrupted, do not leave paint in hoses, spray guns or spray equipment. Flush all equipment thoroughly with thinner. 8. Clean all equipment immediately after use with thinner. Flushing spray equipment periodically during daily work is good practice. Cleaning frequency depends on the volume sprayed, temperature, spraying time, including interruptions, and other factors. 9. Surplus paint and empty containers must be disposed of in accordance with the relevant regional regulations.
20kg
Keep sealed in a ventilated, cool, dry place away from sources of ignition. Minimum 12 months.
1. For the coating and its recommended thinners, see the safety sheets and the safety data of the relevant materials. This is a solvent-borne coating; avoid inhaling spray mist and solvent vapours, and avoid exposing skin and eyes and contact with uncured paint as far as possible. 2. All work related to the application and use of this product must comply with the relevant national health, safety and environmental standards and regulations. 3. If welding or flame cutting is required on metal coated with this product, dust and fumes will be generated; use appropriate personal protective equipment and adequate local ventilation. 4. If in doubt about the suitability of this product, consult the company.
The information provided in this product data sheet is based on laboratory test results that we consider accurate, and is provided for application guidance only. All recommendations and advice given by T&H on the use of T&H products, whether in technical documents, special consultation or otherwise, are based on information we consider most reliable. Our products and the information provided are intended for users with the necessary knowledge and industrial experience, and it is for these end users to determine whether the products are suitable for their use. T&H cannot control the quality and condition of the substrate, nor the various factors affecting the use of the product. Therefore, T&H accepts no liability for any loss, injury or damage arising from the use of our products or from reliance on this product data sheet (unless otherwise agreed in writing). Data in this product data sheet may be revised as necessary based on practical experience and continued product development.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.