Waterborne Coating Byaqua 6400N is a waterborne coating. A two-component waterborne epoxy-polyamide coating tested to nuclear-grade standards. Parameters on this page: volume solids 40% ± 2%, theoretical spreading rate 10 m2/L, number of components: Two-component.
Source: T&H original technical data sheet (TDS) "Waterborne Coating Byaqua 6400N"; values such as spreading rate are converted from the TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 40% ± 2% |
|---|---|
| Dry Film Thickness | 30-70 µm (depending on substrate condition) |
| Theoretical Spreading Rate | 10 m2/L |
| VOC | <100 g/L (mixed) |
| Density / Specific Gravity | 1.25 ± 0.10 kg/L (mixed) |
| Number of Components | Two-component |
| Mixing Ratio | 2.25:1 (by weight) |
| Colour / Appearance | Various colours |
| Gloss | Matt |
Waterborne Yacote Coating
• A two-component waterborne epoxy polyamide coating that has passed nuclear-grade standard tests; • Fast drying and easy to sand; • Hard film with superior durability; • Waterborne product, environmentally friendly throughout the system, low odour, suitable for new construction and repair in confined and poorly ventilated spaces, an ideal environmentally friendly application solution;
(23°C,RH55%,DFT: 40µm)
| Colour | Various colours |
|---|---|
| Gloss | Matt |
| density | 1.25 ± 0.10 kg/L (mixed) |
| Volume Solids | 40 ± 2% (mixed) |
| Mixing Ratio | 2.25:1 (by weight) |
| VOCs | <100 g/L (mixed) |
| Induction Time | None |
| Pot life (30 °C) | 1.5h |
| Theoretical Spreading Rate | 10 m2/L |
| Recommended dry film thickness | 30~70 µm (depending on substrate condition) |
| Drying time* | Surface dry 2 h; fully cured 7 d |
| Recoating interval (25 °C)* | Minimum 24 h, maximum 1 year |
*Ambient temperature/humidity affects the drying time and minimum overcoating interval
Surface preparation: ● Ensure the surface is clean, dry and free from stains; remove laitance and debris by a suitable method, and remove dust;
● A suitable primed surface that has been repaired and dried;
Recommended number of coats: 1-2 coats, 30-70 µm dry film thickness
Substrate/primer: puttied concrete, bare concrete surfaces, mortar surfaces, etc.
| Airless Spray | Thinning 5~10% | Nozzle tip 0.33~0.38 mm | Pressure 15~20 MPa |
| Air Spray | 10~15% | 1.2~2.0mm | 0.3~0.4MPa |
| Roller or brush | 0~5% | -- | |
* When applying on concrete or cement surfaces without putty, the thinning ratio of the first coat should reach 20-25%.
● Wear a mask, gloves and other protective equipment correctly;
● Mix according to the curing ratio, and adjust the thinner amount to mix thoroughly and uniformly;
● The substrate temperature shall be at least 3 °C above the dew point, with a moisture content < 6%;
● The ambient temperature shall be controlled at 5–35 °C, and the relative humidity shall not exceed 85%; where possible, indoor application is preferable to ensure coating appearance
quality.
● All work related to the application and use of this product shall be carried out in accordance with the relevant national health, safety and environmental standards and regulations;
● If in doubt about the suitability of this product, consult the company;
| Base PTA | 11.5L(16.1kg) |
|---|---|
| Curing agent PTB | 6.5L(7.15kg) |
| Storage | ● Store sealed in a ventilated, cool, dry place away from ignition sources; |
● The ideal storage temperature is 5–35 °C, protected from freezing at 0 °C or high temperatures.
| Shelf life | At least 12 months |
|---|
To use the company's products correctly, obtain and read the company's Application Work Instruction;
● The information in this data sheet is based on laboratory test results that we believe to be accurate, and is provided as application guidance only. T&H
for all recommendations and advice on the use of T&H products, whether in technical documents, special consultations or otherwise, are based on information that we believe to be reliable. Our products and the information provided are intended for users with the necessary knowledge and industrial experience; it is ultimately the end user who decides whether the products are suitable for their use. T&H cannot control the quality and condition of the substrate, nor the various factors affecting the use of the product. Therefore, T&H accepts no liability for any loss, injury or damage arising from the use of the company's products or from reliance on this data sheet (unless otherwise agreed in writing).
● The data in this data sheet will be revised as necessary based on practical experience and continuous product development.
Version No.: XHv1.2
Publication date: November 2023
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.