SKSHU FFM650 Silicone Heat-resistant Paint is a heat-resistant coating in the silicone system. Mainly used for anticorrosive protection of steel structures in high-temperature environments, as a primer-topcoat protection coating or as a high-temperature topcoat. Parameters on this page: volume solids 55 ± 2% (aluminium pink 46% ± 2%); dry film thickness 20–50 µm; theoretical spreading rate 27.5/23.
Source: SKSHU 3TREES original technical data sheet (TDS) 'SKSHU FFM650 Silicone Heat-resistant Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 55 ± 2% (aluminium pink 46% ± 2%) |
|---|---|
| Dry Film Thickness | 20–50 µm |
| Theoretical Spreading Rate | 15.3 m2/L |
| VOC | 360 g/L |
| Density / Specific Gravity | Approx. 1.4 kg/L (aluminium shade 1.2 kg/L) |
| Number of Components | — |
| Flash Point | 30°C |
| Thinner | FFX701 Inorganic Zinc Thinner |
| Colour / Appearance | White, aluminium, black |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
SKSHU FFM650 Silicone Heat-resistant Paint
FFM650 is a heat-resistant paint based on silicone resin, withstanding temperatures up to 600 °C, used as a long-term protection coating for hot pipes, exhaust pipes, chimneys and other hot surfaces.
Mainly used for anticorrosive protection of steel structures in high-temperature environments, as a primer-topcoat protection coating or as a high-temperature topcoat.
| Colour: | White, aluminium, black |
|---|---|
| Gloss: | Matt |
| Volume solids: | 55 ± 2% (aluminium pink 46% ± 2%) |
| Specific gravity: | Approx. 1.4 kg/L (aluminium shade 1.2 kg/L) |
| Flash point: | 30°C |
| VOC content: | 360 g/L |
| Storage time: | Dry, cool environment, 12 months |
| Thinner | FFX701 Inorganic Zinc Thinner |
|---|---|
| Recommended dry film thickness: | 20–50 µm |
| Thinner quantity (by volume) | Airless spray <5% | Air spray <20% | Roller or brush <5% |
| Recommended nozzle size | 0.43-0.64mm | 1.5-2.5mm | / |
| Recommended spray pressure | 15-25MPa | 0.3-0.6Mpa | / |
| Application suitability | Recommended | Applicable | Repair |
Theoretical spreading rate (standard colour / aluminium pink versions)
| Dry film thickness (µm) | 20 | 30 | N/A |
| Theoretical spreading rate m²/L | 27.5/23 | 18.3/15.3 | N/A |
*The theoretical spreading rate of the company's products is based on volume solids; divide the data in the table by the specific gravity of each colour version for the theoretical consumption in kg.
| Temperature | Touch dry (h) | Hard dry (h) | Maximum recoat |
| 15°C | 1 | 8 | N/A |
| 25°C | 0.5 | 4 | N/A |
★ After hard dry, the coated component can be handled or assembled; before the component is put into service, it must be heated to 200 °C for 2 hours,
If this product is applied directly to iron substrates, the surface should be clean, dry and uncontaminated; before painting, all surfaces should be assessed and prepared to ISO 8504. Components should be blast-cleaned to Sa 2½ with a surface roughness of 40–75 µm.
Before derusting, remove all oil/grease and weld spatter and smooth welds and sharp edges.
If this product is applied over inorganic zinc, confirm before spraying that the inorganic zinc coating is free of oil and water and fully cured; a mist coat of this product over the inorganic zinc surface is recommended first to seal it.
| FFM650 Silicone Heat-resistant Paint | 5 kg/pail |
|---|
For the coating and its recommended thinners, see the safety sheets and the relevant Material Safety Data Sheet.
This is a solvent-borne coating; use the necessary protective equipment and avoid inhaling spray mist and solvent vapours.
In addition, avoid contact of uncured paint with skin and eyes.
In all cases, SKSHU (3TREES) shall not be liable for any indirect, special, incidental or consequential loss of any kind arising from or in connection with the use of this product (whether based on negligence, strict liability or tort).
The information in this product data sheet is based on laboratory tests we believe to be reliable, and is provided for guidance only. SKSHU (3TREES) may revise this information at any time as experience accumulates and product development progresses.
All recommendations and advice concerning the use of this product, whether in technical documents, in response to an enquiry or otherwise, are given to the best of our knowledge and are believed to be reliable. Our products and related information are provided for industrial users possessing the necessary knowledge and practical skills, and it is the end user's responsibility to determine whether the product is suitable for the specific use. The buyer, having performed such evaluation, proceeds entirely at its own risk.
The quality and condition of the substrate on site, and the many other factors affecting product use and application, are beyond SKSHU (3TREES)'s control.
SKSHU (3TREES) accepts no liability for coating quality problems caused by application environment, application process, surface preparation or personnel operation (unless otherwise provided in a written agreement).
To avoid misuse, confirm with our sales staff that the product data sheet in hand is the latest version.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.