SKSHU (3TREES) FFM200 Aliphatic Fluorocarbon Topcoat belongs to fluorocarbon coatings and is used as a topcoat. Excellent weathering resistance, no chalking, no yellowing, strong gloss and colour retention. Parameters on this page: volume solids 47 ± 2%, dry film thickness 40–100 µm, theoretical spreading rate 9.40 m²/L.
Parameter source: SKSHU (3TREES) original technical data sheet (TDS) “SKSHU (3TREES) FFM200 Aliphatic Fluorocarbon Topcoat”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 47 ± 2% |
|---|---|
| Dry Film Thickness | 40–100 µm |
| Theoretical Spreading Rate | 9.40 m²/L (dry film 50 µm) |
| VOC | 450 g/L |
| Density / Specific Gravity | Approx. 1.4 kg/L (white; other colours vary slightly) |
| Number of Components | Two-component |
| Flash Point | 34 °C |
| Thinner | FFX201 Fluorocarbon Thinner |
| Mixing Ratio | Base FFM200A : curing agent FFM200B = 8.12:1 (by volume) |
SKSHU (3TREES) FFM200 Aliphatic Fluorocarbon Topcoat
SKSHU (3TREES) FFM200 is a two-component aliphatic fluorocarbon resin coating curable at low temperature, particularly suitable for coating and maintenance of steel structures or concrete components in severely corrosive atmospheric environments; provides long-term protection for port machinery, petroleum and petrochemical facilities, bridges, power facilities, airports and stations, banks, television towers, bridges and other structures.
Complies with HG/T3792-2014 "Crosslinked Fluororesin Coatings" requirements.
Excellent weathering resistance, no chalking, no yellowing, strong gloss and colour retention.
Acid and alkali resistance, oil resistance, impact resistance, abrasion resistance, firm adhesion.
| Colour: | White / customer-specified colours |
|---|---|
| Gloss: | Glossy (60–80.60°) |
| Volume solids: | 47±2% |
| Specific gravity: | Approx. 1.4 kg/L (white; other colours vary slightly) |
| Recommended dry film thickness: | 40–100 µm |
| Flash point: | 34 °C |
| Theoretical Spreading Rate | 9.40 m²/L (dry film 50 µm) |
| VOC content: | 450 g/L |
| Fully cured | 7 days |
| Storage time | Dry, cool environment, 12 months |
| Mixing ratio: | Base FFM200A : curing agent FFM200B = 8.12:1 (by volume) |
|---|---|
| Thinner: | FFX201 Fluorocarbon Thinner |
| Thinner | Airless spray 0–5%* | Air spray 0–5%* | Roller or brush 0–5%* |
| Recommended nozzle size | 0.43-0.48mm | 1.0-2.0mm | / |
| Recommended spray pressure | 15-25MPa | 0.3-0.6MPa | / |
| Application suitability | Recommended | Applicable | Repair |
*Thinner improves application viscosity; for spraying, the addition is based on a satisfactory gun test, but must comply with national VOC emission regulations. Airless spray is preferred; roller and brush are suitable for small-area repair only.
| Dry film thickness (µm) | 50 | 75 | 100 |
| Theoretical consumption (L/m²) | 0.11 | 0.16 | 0.21 |
| Theoretical consumption (kg/m²) | 0.15 | 0.23 | 0.31 |
*Practical consumption is affected by equipment, operator technique and application environment; determine the practical consumption according to actual conditions.
Recoat time* Temperature
| 0°C | Minimum (h) 24 | Maximum (days) 60 |
| 10°C | 12 | 30 |
| 20°C | 8 | 14 |
| 30°C | 4 | 7 |
| -- The recoat interval depends on the subsequent exposure conditions | If the maximum recoat interval is exceeded, abrade the primer surface to ensure intercoat adhesion. Surfaces exposed to a contaminated environment must be washed clean with high-pressure fresh water and allowed to dry before recoating. |
|---|
Drying/curing table at 50 µm dry film thickness
| Temperature | Touch dry (h) | Full cure (days) | Pot life (h) |
| 0°C | 4 | 45 | 8 |
| 10°C | 2 | 30 | 4 |
| 20°C | 1 | 14 | 2 |
| 30°C | 0.5 | 7 | 1 |
- Adequate and continuous ventilation must be maintained during application and curing of the coating.
- When applying at ambient air or substrate surface temperatures below 5 °C, pre-warm the mixed paint to above 10 °C.
This product is mainly used as a protective topcoat. All surfaces to be coated shall be clean, dry and free from contamination. Before painting, ensure the previous coat is within its overcoating interval; remove oil and water from the coating surface and remove contaminants. If the coating has suffered mechanical damage and local rusting has occurred, perform local abrasive blasting to Sa2½ or power tool cleaning to St3, and carry out local repair of the previous coat. For paint coatings beyond the overcoating interval, abrade the surface to ensure adhesion.
| FFM200A Aliphatic Fluorocarbon Topcoat: | 24.7 kg/drum |
|---|---|
| FFM200B Aliphatic Fluorocarbon Topcoat Curing Agent | 2.3 kg/drum |
For the coating and its recommended thinners, see the safety sheets and the relevant Material Safety Data Sheet.
This is a solvent-borne coating; use the necessary protective equipment and avoid inhaling spray mist and solvent vapours.
In addition, avoid contact of uncured paint with skin and eyes.
In all cases, SKSHU (3TREES) shall not be liable for any indirect, special, incidental or consequential loss of any kind arising from or in connection with the use of this product (whether based on negligence, strict liability or tort).
The information in this product data sheet is based on laboratory tests we believe to be reliable, and is provided for guidance only. SKSHU (3TREES) may revise this information at any time as experience accumulates and product development progresses.
To the best of our knowledge, the data and information are reliable. Our products and related information are provided exclusively for industrial users possessing the necessary knowledge and practical skills; the end user of the product is responsible for determining whether this product is suitable for its specific use. Therefore, it is believed that the purchaser has carried out such evaluation accordingly and shall have full discretion and bear the corresponding risk.
The quality and condition of the substrate on site, and the many other factors affecting product use and application, are beyond SKSHU (3TREES)'s control. SKSHU (3TREES) accepts no liability for coating quality problems caused by application environment, application process, surface preparation or personnel operation (unless otherwise provided in a written agreement).
To avoid misuse, confirm with our sales staff that the product data sheet in hand is the latest version.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.