3Tree FFM105 One-component Acrylic Topcoat is an acrylic coating used as a topcoat. It offers fast drying and rapid recoating, good flexibility, a tough and abrasion-resistant film, and good water, acid, salt water and ageing resistance. Parameters on this page: volume solids 50 ± 2%, dry film thickness 40–80 µm, theoretical spreading rate 0.25.
Parameter source: 3Tree manufacturer's Technical Data Sheet (TDS) "3Tree FFM105 One-component Acrylic Topcoat"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 50 ± 2% |
|---|---|
| Dry Film Thickness | 40–80 µm |
| Theoretical Spreading Rate | 0.25 L/m2 |
| VOC | ≤ 450 g/L |
| Density / Specific Gravity | Approximately 1.18 ± 0.05 kg/L (grey; other colours vary slightly) |
| Number of Components | One-component |
| Flash Point | 26°C |
| Thinner | Thinner FFX101 |
| Colour / Appearance | White, grey, black (other RAL or GB colours) |
3Tree FFM105 is a one-component, high-solids multi-functional acrylic topcoat with good weatherability, suitable for the surfaces of port machinery, construction machinery and pipelines, and mainly used for new construction and maintenance of outdoor steel structure protection projects exposed to moderate atmospheric corrosion environments.
Fast-drying and rapid recoating; good flexibility, tough and abrasion-resistant film; excellent water, acid, salt water and ageing resistance.
| Colour: | White, grey, black (other RAL or GB colours) |
|---|---|
| Gloss: | To be agreed |
| Volume solids: | 50±2% |
| Specific gravity: | Approx. 1.18±0.05 kg/L (grey; other colours vary slightly) |
| Flash point: | 26°C |
| VOC content: | ≤ 450 g/L |
| Storage time: | Dry, cool environment, 12 months |
| Thinner | Thinner FFX101 |
| Recommended dry film thickness: | 40–80 µm |
| Induction time: | No induction required |
| Thinner quantity | Airless spray 0–5%* | Air Spray 0–30%* | Roller or brush 0–5%* |
| Recommended nozzle size | 0.43mm | 1.5mm | / |
| Recommended spray pressure | 15-25MPa | 0.4-0.6MPa | / |
| Application suitability | Recommended | Repair | |
*Thinner addition improves application viscosity; for spraying, the amount added is based on a satisfactory spray gun test and shall comply with national laws and regulations on VOC emissions. Airless spray is recommended for this product; roller and brush application are suitable only for small-area repair.
| Dry film thickness (µm) | 40 | 60 | 80 |
| Theoretical consumption (L/m²) | 0.12 | 0.19 | 0.25 |
| Theoretical consumption (kg/m²) | 0.2 | 0.3 | 0.4 |
*Practical consumption is affected by equipment, operator technique and application environment; determine the practical consumption according to actual conditions.
Overcoating interval*
| Temperature | Touch Dry min | Hard dry (h) | Pot life (h) | ||
| Minimum (hours) | Maximum (days) | ||||
| 5°C | 60 | 4 | / | 8 | / |
| 15°C | 40 | 3 | / | 6 | / |
| 25°C | 30 | 2 | / | 4 | / |
| 35°C | 10 | 0.5 | / | 2 | / |
| -- The recoat interval depends on the subsequent exposure conditions | If the maximum recoat interval is exceeded, the surface shall be abraded to a rough profile to ensure inter-coat adhesion. Surfaces exposed to polluted environments must be washed clean with high-pressure fresh water and allowed to dry before recoating. |
|---|
The surface to be coated shall be clean, dry and free from contamination. Before painting, abrasive blast cleaning of the substrate is recommended to achieve a cleanliness of Sa2½ and a surface profile of 40–75 µm; before blasting, oil, grease and weld spatter shall be removed completely, and welds and sharp edges ground.
Areas that cannot be blast-cleaned shall be power-tool cleaned to St3, removing loose mill scale, rust and dust; before spraying, the surface shall be free of oil and water.
Where old coatings exist (chemically curing coatings only), the old film shall be abraded, loose paint removed by power tool, and other loose impurities removed; the surface shall be free of oil and water.
20 kg/drum
For the coating and its recommended thinners, see the safety sheets and the relevant Material Safety Data Sheet.
This is a solvent-borne coating; use the necessary protective equipment and avoid inhaling spray mist and solvent vapours.
In addition, avoid contact of uncured paint with skin and eyes.
In all cases, SKSHU (3TREES) shall not be liable for any indirect, special, incidental or consequential loss of any kind arising from or in connection with the use of this product (whether based on negligence, strict liability or tort).
The information in this data sheet is based entirely on our knowledge obtained in the laboratory and in practice. The use of coating products is usually outside our control, so the warranty is limited to the quality of the product itself. To comply with local regulations, the product may be adjusted
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.