Product appearance recommended dry film thickness: matt 200 µm. Colour recommended wet film thickness: grey 345 µm. Composition theoretical spreading rate: two-component for 200 µm dry film: ≅ 600 g/m². Mixing ratio (spreading rate varies with substrate roughness and permeability). Drying time by volume base: 47% for 200 µm dry film. Parameters on this page: components two-component. Comparable products of the same brand: AMERCOAT 114 A Epoxy Filler 114 A, AMERCOAT 220 Water-borne Acrylic Topcoat 220, AMERCOAT 240 SIGMACOVER 240 High-solids Multi-purpose Epoxy 240.
Data source: PPG original Technical Data Sheet (TDS), "HYDRO RENDER Putty"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | — |
|---|---|
| Dry Film Thickness | — |
| Theoretical Spreading Rate | — |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | Water or Thinner No. 1. (1) If the product has dried, use Thinner No. 1 |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
Type/use: water-borne epoxy polyamide filler. Substrate: concrete.
Performance: indoor; outdoor. Used to fill pores, impregnated cracks and other defects on concrete surfaces before painting.
Approved by EDF (Electricité de France), CEMETE, CEA (French Atomic Energy Commission) and BINE; for on-site painting;
laboratories; maintenance;
(Beijing Nuclear Engineering Research and Design Institute) approved for use in nuclear power plants. (PID system). Applicable environment:
Complies with the PMUC specification for general aggressive environments.
Product appearance recommended dry film thickness: matt 200 µm. Colour recommended wet film thickness: grey 345 µm. Composition theoretical spreading rate: two-component for 200 µm dry film: ≅ 600 g/m². Mixing ratio (spreading rate varies with substrate roughness and permeability). Drying time by volume base: 47% for 200 µm dry film:
Hardener: 53%. Dust-free: 1 hour. Touch dry: 6 hours. Thinner: water. Recoatable: none. Epoxy primer 211. Overcoatable: epoxy topcoat 456. Pot life: Shengfuge EAP 2 hours 30 minutes. HYDRO RENDER coating*. Ambient temperature affects pot life and minimum overcoating interval. Lifute 60. Density overcoating interval 1.68 ± 0.05 for 200 µm dry film:
Solids content minimum*: 24 hours - maximum*: 1 year. Service temperature by volume*: 59% ± 2. None. All data related to the density and solids content of the topcoat are based on the product being white. At the same time, these data are based on the mixing of the appropriate products.
*See Overview.
Substrate and surface preparation; substrate type: concrete.
Ensure the surface is clean, dry and free from stains before painting.
Remove laitance and debris by a suitable method. Dust off.
Preparation of the product for use/thinning:
Stir the base mechanically and slowly add the curing agent until thoroughly mixed.
If necessary, thin the product according to the application conditions.
| Thinner: water | Cleaner: water or Thinner No. 1. (1) If the product has dried, use Thinner No. 1. |
|---|
Tool Thinner Nozzle pressure
| Brush, trowel, air spray gun | Not usable, usable, not usable | Not usable, 0/5% |
| High-pressure spray gun | Not available |
Application conditions:
Ambient temperature: +10 °C to +35 °C. Concrete moisture content shall not exceed 8%. Substrate temperature: at least 3 °C above the dew point. Note: good ventilation is required to facilitate moisture evaporation.
Two coats of filler are required:
The first coat removes air bubbles and levels the surface.
After the first coat dries, apply the second coat to smooth the surface.
Health and safety; flash point:
Base and hardener: none. Thinner No. 1: 21 °C < flash point < 55 °C. VOC content: 18 g/L, compliant with European paint and varnish sample criteria.
Packaging and storage. Packaging: 27 kg (base: 13.5 kg / hardener: 13.5 kg). Storage: unopened indoors between +5 °C and +35 °C, can be stored for 12 months. Protect from freezing.
Sigma Coatings (China), Room 408, Baiteng Building, 318 Fuzhou Road, Shanghai 200001. Tel: 021-6391-2991; Fax: 021-6391-2700
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.