TR607 alkyd aluminium heat-resistant paint 200°C is a heat-resistant coating of the alkyd system. Applied to steel surfaces in metallurgy, the machinery industry and insulation engineering, providing heat resistance, rust protection and decoration; the film withstands temperatures up to 200°C and exhibits all the properties common to alkyd coatings. Two-component silver aluminium heat-resistant paint. Parameters on this page: dry film thickness 30 µm, theoretical spreading rate 11.8 m²/kg, number of components: two-component.
Parameter source: OSAKA manufacturer's Technical Data Sheet (TDS) "TR607 Alkyd Aluminium Heat-resistant Paint 200°C (Two-component)"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 40% |
|---|---|
| Dry Film Thickness | 30 µm |
| Theoretical Spreading Rate | 11.8 m²/kg |
| VOC | 519 g/L |
| Density / Specific Gravity | 1.13 kg/L |
| Number of Components | Two-component |
| Flash Point | 35°C |
| Thinner | OUP 102, recommended addition 3%–5% |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
Two-component silver aluminium powder heat-resistant paint.
Used on steel surfaces in metallurgy, the machinery industry and thermal insulation engineering; provides heat resistance, anti-rust and decorative effects; the paint withstands temperatures up to 200°C and has all the properties of general alkyd paints.
| Volume Solids | 40% |
|---|---|
| Dry Film Thickness | 30 µm corresponds to 75 µm WFT |
| Theoretical Spreading Rate | 11.8 m²/kg |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 519 g/L |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
|---|---|
| Airless spray | Recommended: nozzle tip size 0.43–0.53 mm; fluid pressure ≥17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable, but not recommended. |
| Thinner | OUP 102, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 102 |
| Pot life | 23°C–12 h |
| Drying Time | ||||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 10°C | 4 | 36 | 36 h | Unlimited |
| 23°C | 2 | 24 | 24 h | Unlimited |
| 35°C | 1 | 18 | 18 h | Unlimited |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Part A: 16 kg in a 20 L pail; Part B: 4 kg in a 4 L pail |
| Flash Point | 35°C |
| density | 1.13 kg/L |
Before application, all surfaces to be coated shall be assessed and prepared in accordance with ISO standards. If grease is present, clean with solvent to SSPC-SP1, abrasive blast clean to Sa2.5 or power tool clean to St3, and remove dust and dirt.
Recommended number of coats: two coats by high-pressure airless spray, dry film thickness reaching 60 µm.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.