EPTANK364 Epoxy Phenolic Tank Lining belongs to Epoxy. Suitable for internal wall anti-corrosion of commercial storage tanks and vessels at crude oil terminals. Two-pack, various colours, tank lining. Parameters on this page: dry film thickness 100 µm, theoretical spreading rate 4.64 m²/kg, number of components two-component.
Parameter source: OSAKA original technical data sheet (TDS) “EPTANK364 Epoxy Phenolic Tank Lining”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 65% |
|---|---|
| Dry Film Thickness | 100µm |
| Theoretical Spreading Rate | 4.64 m²/kg |
| VOC | 301 g/L |
| Density / Specific Gravity | Approx. 1.40 kg/L |
| Number of Components | Two-component |
| Thinner | OUP 103, recommended addition 3%–5% |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
| Pot Life | 23 °C: 1 h |
Two-pack, various colours, tank lining
Suitable for internal wall anti-corrosion of commercial storage tanks and vessels at crude oil terminals.
| Volume Solids | 65% |
|---|---|
| Dry Film Thickness | 100 µm corresponds to 185 µm wet film thickness. |
| Theoretical Spreading Rate | 4.64 m²/kg, based on 100 µm dry film thickness. |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 301 g/L |
| Mixing Ratio | Component A : Component B = 4:1 (by weight) |
|---|---|
| Airless spray | Recommended: tip size 0.53–0.68 mm; fluid pressure ≥ 19 MPa |
| Brush or roller | For small areas only, including touch-up; repeat application is required to achieve the specified film thickness. |
| Conventional spray | Suitable but not recommended. |
| Thinner | OUP 103, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 103 |
| Induction period | 15 min |
| Pot life | 23 °C: 1 h |
| Drying Time | ||||
| Substrate Temperature | Touch dry (h) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 6 | 48 | 24 h | 21 days |
| 23°C | 3 | 24 | 16 h | 14 days |
| 35°C | 1 | 16 | 12 h | 10 days |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | Component A: 16 kg in a 20 L container; Component B: 4 kg in a 4 L container |
| Flash Point | Above 23 °C |
| density | Approx. 1.40 kg/L |
Consult the company for detailed information on coating of tank internal walls. Remove grease by solvent cleaning in accordance with SSPC-SP1; where necessary, remove weld spatter, grind welds and sharp edges smooth, and blast to white metal (SSPC-SP10 or ISO 8501:2007 Sa2.5). Apply this paint before oxidation occurs; if oxidation has occurred, re-blast the oxidized areas to the specified standard. Ensure the surface is clean before application, and apply the subsequent coat of this paint within the specified recoat interval. Hot water tank: if slight rusting is present on the internal walls of the hot water tank, blast to Sa1 in accordance with ISO 8501:2007, rinse with clean water, and after drying blast to Sa2.5.
Consult the company to confirm whether this product is suitable for the substance to be stored. This product cannot cure below 5 °C; for proper curing, the steel temperature should be above 10 °C and at least 3 °C above the dew point, with relative air humidity not exceeding 80%.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.