ACP1006 Acrylic Iron Oxide Red Primer/Intermediate Coat is an acrylic paint, used as a primer. Suitable for use as a primer or intermediate coat on construction machinery, machine tools, motors, hardware and building steel structures. A single-component primer or intermediate coat, iron red, fast-drying, applicable at low temperatures, resistant to weak chemical splashes, with excellent anti-corrosion properties. Parameters on this page: volume solids approx. 56%, dry film thickness 40–80 µm, theoretical spreading rate 8.62 m²/kg.
Data source: OSAKA original Technical Data Sheet (TDS), "ACP1006 Acrylic Iron Oxide Red Primer/Intermediate Coat"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 56% |
|---|---|
| Dry Film Thickness | 40–80 µm |
| Theoretical Spreading Rate | 8.62 m²/kg |
| VOC | 378 g/L |
| Density / Specific Gravity | Approx. 1.30 kg/L |
| Number of Components | One-component |
| Flash Point | >28°C |
| Thinner | OUP 110, recommended addition 3%–5% |
| Mixing Ratio | Single pack |
A single-component primer or intermediate coat, iron red, fast-drying, applicable at low temperatures, resistant to weak chemical splashes, with excellent anti-corrosion properties.
Suitable for use as a primer or intermediate coat on construction machinery, machine tools, motors, hardware and building steel structures.
| Volume Solids | Approx. 56% |
|---|---|
| Dry Film Thickness | 40–80 µm |
| Theoretical Spreading Rate | 8.62 m²/kg, based on 50 µm dry film thickness. |
| Practical Spreading Rate | Allowing a suitable loss |
| Volatile organic compound content | 378 g/L |
| Mixing Ratio | Single pack |
|---|---|
| Airless spray | Recommended: tip size 0.43–0.53 mm; fluid pressure ≥ 17.6 MPa |
| Brush or roller | Recommended |
| Conventional spray | Suitable but not recommended. |
| Thinner | OUP 110, recommended addition 3%–5%. |
| Paint equipment cleaner | OUP 110 |
| Pot life | Unlimited |
| Drying Time | ||||
| Substrate Temperature | Touch dry (min) | Hard dry (h) | Recoat Interval | |
| Minimum | Maximum | |||
| 5°C | 30 | 24 | 24 h | Unlimited |
| 23°C | 20 | 12 | 12 h | Unlimited |
| 35°C | 3 | 4 | 4 h | Unlimited |
| Storage | Store in a cool, dry environment |
|---|---|
| Shelf life | 1 year |
| Packaging Specifications | 25 kg in a 20 L drum |
| Flash Point | >28°C |
| density | Approx. 1.30 kg/L |
As a primer: new steel structures must be blast cleaned to Sa 2.5 or power tool cleaned to St 3, oil removed with solvent, and the surface kept clean and dry. As an intermediate coat: suitable preceding coats include epoxy primers, chlorinated rubber primers, vinyl primers etc., with the surface kept clean and dry; the suitable subsequent coat is an acrylic resin topcoat.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.