Local exposed areas, immersed areas, internal areas or other areas of the vessel (welds, edges, corners). For areas susceptible to severe corrosion or already corroded and pitted, a single coat can be applied to provide high-performance rust protection. Parameters on this page: volume solids 90 ± 2%, theoretical spreading rate 0.90 m²/L (1 mm), component count two-component.
Parameter source: nippon-marin manufacturer's Technical Data Sheet (TDS) "NEOGUARD BULCON Surface-tolerant Pure Epoxy Anti-corrosion Coating"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 90 ± 2% |
|---|---|
| Dry Film Thickness | 1.0-2.0mm |
| Theoretical Spreading Rate | 0.90 m²/ℓ (1 mm) |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | Refer to note 3) |
| Mixing Ratio | Base : curing agent = 3.2 : 1.8 |
| Colour / Appearance | Pale cream base — EED352, curing agent — EED304 |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Ultra-high-build, surface-tolerant, two-component pure epoxy anti-corrosive paint with excellent wetting of the substrate; it can be applied directly to manually prepared surfaces or to existing coatings for maintenance and repair, and to virtually any area. On areas prone to severe corrosion or already corroded and pitted, a single coat provides high-performance anti-corrosive protection.
Local exposed areas, immersed areas, internal areas or other areas of the vessel (welds, edges and corners).
| Type | Pure epoxy (ultra-high-build/surface-tolerant/two-component) |
|---|---|
| Colour | Pale cream base — EED352, curing agent — EED304 |
| Gloss | Flat |
| Solids content (by volume) | 90 ± 2% (ISO3233:1998) |
| Mixing ratio (by weight) | Base : curing agent = 3.2 : 1.8 |
| Recommended film thickness | Dry film: 1.0–2.0 mm |
| Wet film | 1.1 ~ 2.2mm |
| Theoretical Spreading Rate | 0.90 m²/ℓ (1 mm) |
| Thinner | Refer to note 3) |
| 5°C | 20°C | 30°C | ||
| Drying Time | Surface Dry | 4 h | 2 h | 1 h |
| Hard Dry | 48 h | 16 h | 8 h | |
| Fully cured | 14 days | 7 days | 5 days | |
| Recoat interval | Minimum | 48 h | 24 h | 16 h |
| (self-recoat) | Maximum | 7 days | 5 days | 3 days |
| Pot life | 2 h | 1 h | 30 min |
| Flash Point | Base 24 °C, curing agent 28 °C |
|---|
Brush/trowel
Remove rust and loose coating with wire brushes, chipping hammers, power wire brushes and abrasive discs. All surfaces to be painted shall be clean, dry and free from contaminants. High-pressure fresh water washing to remove all grease, soluble salts and foreign matter.
| Packaging Specifications | 5 kg (Base 3.2 kg, Hardener 1.8 kg) |
|---|
Take the necessary protective measures to avoid skin and eye contact (e.g. gloves, safety glasses, face
1) The content of this product data sheet may be revised at any time as our experience grows and the product is further developed.
2) Mix the Base and Hardener thoroughly in the specified ratio with a stirrer and scraper.
3) To ensure film thickness, no thinner is added in principle.
4) Pot life 1 h at 20°C. Under high summer temperatures, mix only the quantity required for application.
5) Apply with brush/scraper and ensure the specified film thickness (1 mm) is achieved.
6) Store in the paint warehouse.