Chlorinated Rubber Topcoat J43-32 is a chlorinated rubber paint for use as a topcoat. Suitable for the waterline, hull, superstructure of vessels, as well as power plants, steel plants, wharf steel structures, chemical plants, bridges, containers, hydraulic steel gates, factory buildings, outer walls of petroleum storage tanks, dry gas holders and various other onshore steel structure surfaces for protection and decoration as a topcoat. A high-performance chlorinated rubber topcoat composed of chlorinated rubber, plasticizer, titanium dioxide, colouring pigments, additives and solvents.
Parameter source: KAILIN original technical data sheet (TDS) “Chlorinated Rubber Topcoat J43-32”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 42 ± 3% |
|---|---|
| Dry Film Thickness | 70 µm |
| Theoretical Spreading Rate | 234 g/m² |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | — |
| Flash Point | 31°C |
| Drying Time | Touch dry ≤ 2 h; hard dry ≤ 12 h |
| Packaging Specifications | 20 L drum, 24 kg |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
| Composition | A high-performance Chlorinated Rubber Topcoat composed of chlorinated rubber, plasticizer, titanium dioxide, colouring pigments, additives and solvents. |
|---|
Low permeability of water vapour and oxygen through the film; excellent water resistance, corrosion protection and decorative properties
Excellent low-temperature application properties; may be applied at -20 °C to 50 °C
Film layers dissolve into one another, with excellent intercoat adhesion; on old chlorinated rubber paint
When recoating for maintenance, the firmly adhered old film need not be removed, making maintenance convenient
Suitable for the waterline, hull, superstructure of vessels, as well as power plants, steel plants, wharf steel structures, chemical
plants, bridges, containers, hydraulic steel gates, factory buildings, outer walls of petroleum storage tanks, dry gas holders
and various other onshore steel structure surfaces for protection and decoration as a topcoat.
| Product code | Colour and Appearance | |
| J43-32(605-3) | 08-22 | Orange yellow, semi-gloss |
| J43-32(610-3) | 08-24 | Bean green, semi-gloss |
| J43-32(626) | 08-28 | Iron red, semi-gloss |
| J43-32(626-3) | 08-30 | Iron red, semi-gloss |
| J43-32(629) | 08-31 | Green, semi-gloss |
| J43-32(629-3) | 08-33 | Green, semi-gloss |
| J43-32(634-3) | 08-35 | Scarlet, semi-gloss |
| J43-32(662-3) | 08-38 | Orange red, semi-gloss |
| J43-32(663) | 08-39 | Steel grey, semi-gloss |
| J43-32(663-3) | 08-40 | Steel grey, semi-gloss |
| J43-32(667-3) | 08-42 | White, semi-gloss |
| J43-32(669) | 08-43 | Blue grey, semi-gloss |
| J43-32(670) | 08-46 | Light grey, semi-gloss |
| J43-32(670-3) | 08-47 | Light grey, semi-gloss |
| J43-32(671-3) | 08-49 | Sea blue, semi-gloss |
| J43-32(675-3) | 08-51 | Medium grey, semi-gloss |
| J43-32(682-3) | 08-53 | Black, semi-gloss |
| Product code | Volume solids* | Dry Film Thickness | Wet Film Thickness | Theoretical quantity |
| % | µm | g/m² | ||
| 605-3 | 44±3 | 70 | 158 | 222 |
| 610-3 | 42±3 | 70 | 168 | 236 |
| 626 | 42±3 | 40 | 95 | 121 |
| 626-3 | 42±3 | 70 | 167 | 234 |
| 629 | 42±3 | 40 | 95 | 121 |
| 629-3 | 42±3 | 70 | 167 | 234 |
| 634-3 | 42±3 | 70 | 167 | 234 |
| 662-3 | 42±3 | 70 | 167 | 234 |
| 663 | 40±3 | 40 | 100 | 127 |
| 663-3 | 42±3 | 70 | 167 | 234 |
| 667-3 | 42±3 | 70 | 167 | 234 |
| 669 | 42±3 | 40 | 95 | 121 |
| 670 | 42±3 | 40 | 95 | 121 |
| 670-3 | 42±3 | 70 | 167 | 234 |
| 671-3 | 42±3 | 70 | 167 | 234 |
| 675-3 | 42±3 | 70 | 167 | 234 |
| 682-3 | 42±3 | 70 | 167 | 234 |
* Volume solids (determined according to GB/T9272 eqv ISO3233:1998)
| Flash Point | 31°C |
|---|---|
| Drying time (25 °C) | Touch dry ≤ 2 h; hard dry ≤ 12 h |
| Recoat interval | |||
| Temperature | 5°C | 20°C | 30°C |
| Minimum | 24h | 12h | 6h |
| Maximum | Unlimited |
|---|---|
| Recommended number of coats | 1–2 coats, dry film thickness 70–140 µm. High-pressure airless spray is preferred during application. |
615-1, 615-2 aluminium chlorinated rubber anti-rust paint as anti-rust primer, 616 chlorinated rubber iron oxide thick
The micaceous iron oxide anticorrosive paint is used as an intermediate coat, or H06-4 epoxy zinc-rich anticorrosive paint is used as the primer and 842 epoxy
Micaceous iron oxide anticorrosive paint is used as an intermediate coat.
| Application method | Airless Spray Thinner 101 Thinner Dilution 0–5% (by paint weight) Nozzle Tip Size 0.4–0.5 mm Nozzle Pressure 15–20 MPa (approx. 150–200 kg/cm²) Air Spray Thinner 101 Thinner Dilution 0–10% (by paint weight) Nozzle Tip Size 2.0–3.0 mm Air Pressure 0.3–0.4 MPa (approx. 3–4 kg/cm²) |
|---|
A single coat cannot achieve the recommended dry film thickness Thinner 101 Thinner Dilution 0–3% (by paint weight)
| Cleaning solvent | Thinner 101 |
|---|---|
| Safety measures | See the Safety Data Sheet (MSDS) of Shanghai Kailin Paint Factory. |
| Packaging | 20 L drum, 24 kg |
| Shelf Life | 12 months |
| Notes | To use this product correctly, read the Application Guide in this data sheet carefully. |
The above information and data for this product are accumulated from our tests and practical experience
accumulated, and may serve as an application guide. For application carried out under conditions unknown to us, we
We guarantee only the quality of the paint itself and accept no responsibility for other matters. We
and reserve the right to make modifications as the product is improved.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.