Aluminium Phenolic Enamel F04-1 is a phenolic coating used as a topcoat. Suitable for use as a topcoat on all indoor and outdoor wood, metal and other surfaces of construction projects, vehicles and machinery. A topcoat with metallic lustre, made from drying vegetable oil and modified phenolic resin as binder, compounded with aluminium powder. Parameters on this page: volume solids 44 ± 3%, dry film thickness 35 µm, theoretical spreading rate 72 g/m².
Source: KAILIN original technical data sheet (TDS) "Aluminium Phenolic Enamel F04-1"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 44 ± 3% |
|---|---|
| Dry Film Thickness | 35µm |
| Theoretical Spreading Rate | 72 g/m² |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Flash Point | 35°C |
| Thinner | Thinner 104 |
| Colour / Appearance | Aluminium, gloss |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
| Composition | A topcoat with metallic lustre, made from drying vegetable oil and modified phenolic resin as binder, compounded with aluminium powder. |
|---|
Suitable for all indoor and outdoor wood, metal and other surfaces of construction projects, vehicles and machinery
for use as a topcoat.
| Appearance | Aluminium, gloss |
|---|
Component A : Component B = 4:1 (by weight)
| Volume Solids | 44 ± 3% (measured according to GB/T 9272 eqv ISO 3233:1998) |
|---|---|
| Dry Film Thickness | 35µm |
| Wet Film Thickness | 80µm |
| Theoretical quantity | 72g/m² |
| Flash Point | 35°C |
| Drying time (25 °C) | Touch dry ≤ 6 h; hard dry ≤ 18 h |
| Recoat interval | |||
| Temperature | 5°C | 20°C | 30°C |
| Minimum | 48h | 24h | 20h |
| Maximum | Unlimited | ||
| Recommended number of coats | 2 coats, dry film thickness 70 µm |
|---|
711 Red Lead Oleoresinous Anticorrosive, 712 Red Lead Phenolic Anticorrosive, 725 Zinc Yellow Phenolic Anticorrosive,
706 Anticorrosive, C53-38 Aluminium Iron Anticorrosive and other oleoresinous, alkyd and phenolic anticorrosive primers.
Before use, add the aluminium silver paste to the paint per the ratio, stir thoroughly, strain through a 0.2 mm (80 mesh) copper gauze, then use.
| Airless Spray | |
| Thinner | Thinner 104 |
| Thinning quantity | 0–5% (by paint weight) |
| Nozzle tip size | 0.4-0.5mm |
| Spray output pressure | 12–15 MPa (approx. 120–150 kg/cm²) |
| Air Spray | |
| Thinner | Thinner 104 |
| Thinning quantity | 0–10% (by paint weight) |
| Nozzle tip size | 2.0-3.0mm |
| Air pressure | 0.3–0.4 MPa (approx. 3–4 kg/cm²) |
| Roller/brush | Thinner 104; thinning quantity 0–3% (by paint weight) |
|---|---|
| Cleaning solvent | Thinner 104 |
| Safety measures | See the Safety Data Sheet (MSDS) of Shanghai Kailin Paint Factory. |
| Packaging | Component A 20 L drum 16 kg, Component B 4 L drum 4 kg |
| Shelf Life | 12 months |
| Notes | For correct use of this product, carefully read the "Application Guide" in this datasheet. |
The above information and data for this product are accumulated from our tests and practical experience
accumulated, and may serve as an application guide. For application carried out under conditions unknown to us, we
we guarantee only the quality of the paint itself and accept no responsibility for other matters. We
We reserve the right to make modifications as the product is improved.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.