Aluminium Iron Anticorrosive C53-38 is a primer. Suitable as an anticorrosive primer for ships above the waterline, ordinary compartments and general onshore steel structures. Based on alkyd resin and phenolic vehicle, composed of iron oxide red, aluminium powder and other anticorrosive pigments, extender pigments, driers, additives and solvent. Produces no toxic gases during welding, cutting or flame straightening. Parameters on this page: volume solids 48 ± 3%, dry film thickness 40 µm, theoretical spreading rate 106 g/m².
Source: KAILIN original technical data sheet (TDS) "Aluminium Iron Anticorrosive C53-38"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 48 ± 3% |
|---|---|
| Dry Film Thickness | 40µm |
| Theoretical Spreading Rate | 106 g/m² |
| VOC | — |
| Density / Specific Gravity | — |
| Number of Components | — |
| Flash Point | 35°C |
| Thinner | Thinner 104 |
| Colour / Appearance | Silver red, smooth film with slight brush marks |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Based on alkyd resin and phenolic vehicle, composed of iron oxide red, aluminium powder and other anticorrosive pigments, extender pigments,
driers, additives and solvent.
Produces no toxic gases during welding, cutting or flame straightening
| Use | Suitable as an anticorrosive primer for ships above the waterline, ordinary compartments and general onshore steel structures. |
|---|---|
| Appearance | Silver red, smooth film with slight brush marks. |
| Volume Solids | 48 ± 3% (determined per GB/T 9272 eqv ISO 3233:1998) |
|---|---|
| Dry Film Thickness | 40µm |
| Wet Film Thickness | 83µm |
| Theoretical quantity | 106g/m² |
| Flash Point | 35°C |
| Drying time (25 °C) | Touch dry ≤ 3 h; hard dry ≤ 24 h |
| Recoat interval | |||
| Temperature | 5°C | 20°C | 30°C |
| Minimum | 36h | 24h | 20h |
| Maximum | 3 months | ||
| Recommended number of coats | 2 coats, dry film thickness above 80 µm |
|---|---|
| Subsequent coat | Various alkyd or phenolic topcoats |
Mill-scale-free steel: prepare to St3 with pneumatic or power grinding tools
Shop-primed steel: re-prepare damaged and rusted film areas, abrading to St 3
Welded, flame-cut or heat-corrected areas: grind to St 3
| Airless Spray | |
| Thinner | Thinner 104 |
| Thinning quantity | 0–5% (by paint weight) |
| Nozzle tip size | 0.4-0.5mm |
| Spray output pressure | 12–15 MPa (approx. 120–150 kg/cm²) |
| Air Spray | |
| Thinner | Thinner 104 |
| Thinning quantity | 0–10% (by paint weight) |
| Nozzle tip size | 2.0-3.0 mm |
| Air pressure | 0.3–0.4 MPa (approx. 3–4 kg/cm²) |
| Roller/brush | Thinner 104; thinning quantity 0–3% (by paint weight) |
|---|---|
| Cleaning solvent | Thinner 104 |
| Safety measures | See the Safety Data Sheet (MSDS) of Shanghai Kailin Paint Factory. |
| Packaging | 20 L drum, 24 kg |
| Shelf Life | 12 months |
| Notes | To use this product correctly, read the Application Guide in this data sheet carefully. |
The above information and data for this product are accumulated from our tests and practical experience
accumulated, and may serve as an application guide. For application carried out under conditions unknown to us, we
We guarantee only the quality of the paint itself and accept no responsibility for other matters. We
and reserve the right to make modifications as the product is improved.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.