Jotamastic 80 MIO Surface-tolerant Epoxy MIO Primer is an epoxy coating for use as a primer. Industrial protective coatings segment: recommended for offshore environments such as refineries, power stations, bridges, buildings, mining equipment and general structural steel. In atmospheric and immersed environments it may be used as primer, intermediate coat, topcoat or one-coat system. Parameters on this page: volume solids 79 ± 2%, dry film thickness 75-200 µm, theoretical spreading rate 10.5-4 m²/L. Comparable models from the same brand: Barrier 65 S Epoxy Zinc-rich Primer, Barrier 65 Epoxy Zinc-rich Primer, Barrier 75 CN Epoxy Zinc-rich Primer.
Parameter source: JOTUN manufacturer technical data sheet (TDS) Jotamastic 80 MIO Surface-tolerant Epoxy MIO Primer; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 79 ± 2% |
|---|---|
| Dry Film Thickness | 75–200 µm |
| Theoretical Spreading Rate | 10.5-4 m²/L |
| VOC | 265 g/L |
| Density / Specific Gravity | 1.62 kg/L |
| Number of Components | Two-component |
| Flash Point | 35 °C |
| Thinner | JOTUN Thinner No. 17 |
| Mixing Ratio | 7 parts : 1 part : 4 parts : 1 part (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Surface-tolerant Epoxy MIO Primer (0VY)
This is a two-component, polyamine-cured surface-tolerant epoxy coating. A surface-tolerant, micaceous iron oxide pigmented, high solids product.
Designed for areas where ideal surface preparation cannot be achieved or is not required. In atmospheric and immersed environments it may be used as primer, intermediate coat, topcoat or one-coat system.
Suitable for suitably prepared carbon steel and aged coated surfaces. Can be applied at surface temperatures below 0°C.
General:
Mainly for maintenance and repair.
Industrial protective coatings:
Recommended for offshore environments such as refineries, power stations, bridges, buildings, mining equipment and general structural steel.
Others
Jotamastic 80 — Surface-Tolerant Epoxy Primer (0AR)
For the different products in this series, refer to the respective technical data sheets
Grey, black
Property Test/Standard Description
Ambient-curing
| Volume Solids | ISO 3233 | 79± 2 % |
| Gloss (GU 60°) | ISO 2813 | Semi-gloss (35–70) |
| Flash Point | ISO 3679 Method 1 | 35 °C |
| Density | Theoretical Value | 1.62 kg/L |
| VOC — EU | IED (2010/75/EU) (theoretical value) | 265 g/L |
Winter grade
| Volume Solids | ISO 3233 | 72± 2 % |
| Flash Point | ISO 3679 Method 1 | 31 °C |
| Density | Theoretical Value | 1.57kg/L |
| VOC — EU | IED (2010/75/EU) (theoretical value) | 293 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
All data apply to the mixed paint only.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 75–200 µm |
| Wet Film Thickness | 95–250 µm |
| Theoretical Spreading Rate | 10.5 - 4 m²/L |
| Dry Film Thickness | 75–200 µm |
| Wet Film Thickness | 105–280 µm |
| Theoretical Spreading Rate | 9.6–3.6 m²/L |
To ensure lasting adhesion of the next coat, all surfaces must be clean, dry and free of contaminants.
Surface Preparation
| Substrate | Minimum | Recommended | |
| Carbon steel St2 (ISO 8501-1) | Sa 2 (ISO 8501-1) | ||
| Shop-primed Steel: clean, dry and intact shop primer (complying with ISO 12944-5 6.1). | |||
| Coated surface; clean, dry and intact compatible primer (compliant with ISO | Clean, dry and intact compatible primer (compliant with ISO | ||
| 12944-5 | clause 6.1). | 12944-5 | clause 6.1). |
This product may be applied by the following methods
| Spray: | Apply by airless spray. |
| Brush: | usable. Take care to achieve the specified dry film thickness. |
| Roller: |
| Surface-tolerant Epoxy MIO Primer, Component A | 7 parts |
| Surface-tolerant Epoxy Primer, Component B | 1 part |
| Surface-tolerant Epoxy MIO Primer, Component A | 4 parts |
| Surface-tolerant Epoxy Primer, Component B (winter grade) | 1 part |
| Thinner | JOTUN Thinner No. 17 |
|---|
| Nozzle tip size (inch/1000): | 19-25 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
Substrate temperature -5 °C 0 °C 5 °C 10 °C 23 °C 40 °C Ambient-curing
| Touch Dry | 8 h | 4 h | 2 h |
| Walk-on Dry | 24 h | 10 h | 4 h |
| Minimum recoat interval | 24 h | 10 h | 4 h |
| Dry/cured to service | 14 days | 7 days | 2 days |
| Touch Dry | 24 h | 18 h | 12 h | 6 h | 2.5 h |
| Walk-on Dry | 48 h | 26 h | 18 h | 12 h | 5 h |
| Minimum recoat interval | 48 h | 26 h | 18 h | 12 h | 5 h |
| Dry/cured to service | 21 days | 14 days | 7 days | 3 days | 2 days |
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Maximum overcoating interval, atmospheric environment: the maximum time within which the next coat can be applied without any surface preparation.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Standard grade, induction time | 10 min |
| Pot Life | 2 h |
| Winter grade Pot life | 1 h |
Temperature
| Drying, atmospheric | Continuous 90 °C | Peak 90 °C |
| Immersed, sea water | 50 °C | 60 °C |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Note: this coating can withstand different immersion temperatures, depending on the specific chemical and whether immersion is continuous or intermittent. Heat resistance is affected by the coating system as a whole.
When used with other coatings, ensure that all coatings in the system have similar heat resistance.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy shop primer, inorganic zinc silicate shop primer, zinc epoxy, epoxy, modified epoxy, inorganic zinc silicate |
| Subsequent coat: | Polyurethane, epoxy, acrylic, vinyl epoxy |
| Volume | Container Size | |
| (L) | ||
| Surface-tolerant Epoxy MIO Primer, Component A | 16 | 20 |
| Surface-tolerant Epoxy Primer, Component B | 2.3 | 3 |
| Surface-tolerant Epoxy Primer, Component B (winter grade) | 4 | 5 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| Surface-tolerant Epoxy MIO Primer, Component A | 48 months |
| Surface-tolerant Epoxy Primer, Component B | 48 months |
| Surface-tolerant Epoxy Primer, Component B (winter grade) | 36 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge.
Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling, products may show slight colour variation from batch to batch. Likewise, fading and chalking may occur when exposed to sunlight.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.