Intertuf 362 Epoxy Anti-corrosive Paint belongs to epoxy coatings and is used as a primer. A high-performance anti-corrosive paint suitable for use from keel to rail. An abrasion-resistant, surface-tolerant, two-component epoxy primer that can be applied in winter at temperatures as low as -5 °C. Parameters on this page: volume solids 67% ± 2%, dry film thickness 150 µm, theoretical spreading rate 4.47 m²/L. Comparable products from the same brand: Interbond 201 - Temperate Epoxy Primer, Interbond 808 Epoxy Anti-corrosive Paint, Intergard 5101 Epoxy Universal Primer.
Parameter source: International INTERNATIONAL original technical data sheet (TDS) "Intertuf 362 Epoxy Anti-corrosive Paint"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 67% ± 2% |
|---|---|
| Dry Film Thickness | 150 µm |
| Theoretical Spreading Rate | 4.47 m²/L |
| VOC | 283 g/L (as supplied) (EPA Method 24) 199 g/kg (… |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Mixing Ratio | Component A : Component B = 3.00:1 (by volume) |
| Colour / Appearance | KHA323 red, KHA322 grey (North America only) |
| Gloss |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
A wear-resistant, surface-tolerant, two-component epoxy primer suitable for application in winter at temperatures as low as -5 °C.
A high-performance anti-corrosive paint for use from keel to railing.
Suitable for use with impressed current cathodic protection.
For newbuilding, maintenance and repair, or in-service maintenance.
| Colour | KHA323 red, KHA322 grey (North America only) |
|---|---|
| Topcoat/gloss | Gloss |
| Component B (curing agent) | KHA362 |
| Volume Solids | 67% ±2% (ISO 3233:1998) |
| Mixing ratio | Component A : Component B = 3.00:1 (by volume) |
| Standard film thickness | 150 µm DFT (224 µm WFT) |
| Theoretical Spreading Rate | Theoretical spreading rate at 150 µm DFT is 4.47 m²/L, allowing for appropriate loss factors |
| Application Methods | Airless spray, brush, roller |
| Flash Point | Component A 25 °C; Component B 24 °C; after mixing 27 °C |
| Induction Time | Not required |
| Drying data | -5°C | 5°C | 25°C | 35°C |
| Touch dry [ISO 9117/3:2010] | 4 h | 2.5 h | 60 min | 45 min |
| Hard dry [ISO 9117-1:2009] | 24 h | 12 h | 4 h | 2.5 h |
| Pot life after mixing | 6 h | 5 h | 2 h | 60 min |
| Recoat data — see the “Limitations” section | Substrate Temperature |
|---|
| When recoating the following products | -5 °C minimum | -5 °C maximum | -5 °C minimum | 5 °C maximum | 25 °C minimum | 25 °C maximum | 35 °C minimum | 35 °C maximum |
| Interbond 201 | 24 h | 14 days | 12 h | 14 days | 4 h | 14 days | - | |
| Intergard 263 | 24 h | 14 days | 12 h | 14 days | 4 h | 14 days | 2.5 h | 14 days |
| Intergard 282 | 24 h | 14 days | 12 h | 14 days | 4 h | 14 days | - | |
| Intergard 740 | - | 12 h | 7 days | 4 h | 7 days | 2.5 h | 7 days | |
| Intertuf 362 | 24 h | 15 days | 12 h | 15 days | 4 h | 15 days | 2.5 h | 15 days |
| Note | The above recoat data for Interbond 201 apply to the low-temperature type only. |
|---|
| Volatile Organic Compounds | 283 g/L (as supplied) (EPA Method 24); 199 g/kg (as supplied liquid paint). EU Solvent Emissions Directive (Council Directive 1999/13/EC) 248 g/L; Chinese national standard GB23985. VOC values are typical values provided for reference only. They may vary with factors such as colour and normal manufacturing tolerances. |
|---|
Coating hazards GB 30981.2-S-Pb≤1000-NC; complies with GB 30981.2-2025
For the paint system best suited to the surface to be protected, consult your local International Paint representative.
Applied in accordance with the standard Worldwide Marine Specifications.
All surfaces to be coated must be clean, dry and free of contaminants.
Wash with high-pressure or ordinary fresh water as appropriate, and remove all oil, grease, soluble contaminants and other foreign matter in accordance with the SSPC-SP1 solvent cleaning standard.
When used as a temporary primer to protect blasted surfaces, Intertuf 362 may be applied over Intergard 269. The primer surface shall be dry and free from all contamination, and Intertuf 362 must be applied within the specified recoat interval (refer to the Intergard 269 product data sheet).
On newbuildings, remove weld spatter and grind welds and sharp edges smooth where required.
Welds and damaged areas of shop primer must be blast cleaned to Sa 2.5 (ISO 8501-1:2007) or prepared with power tools to Pt3 (JSRA SPSS:1984).
Intact, approved shop primer must be clean, dry and free of soluble salts and any other surface contaminants.
Unapproved shop primer must be fully blast cleaned to Sa 2.5 (ISO 8501-1:2007). In some cases, sweep blasting to a specified International Paint standard (e.g. AS2 or AS3) is acceptable. For specific advice, consult your local International Paint representative.
Major repair: abrasive blast cleaning to Sa2 (ISO 8501-1:2007). If oxidation has occurred between blasting and application of Intertuf 362, the surface shall be re-blasted to the specified pictorial standard.
Surface defects exposed by abrasive blasting must be ground, filled or treated by a suitable method.
Intertuf 362 may be applied to surfaces prepared to International Paint ultra-high-pressure water jetting standard HB2, with flash rust not exceeding standard HB2M. Ultra-high-pressure water jetting is recommended only for the underwater hull, topside and above-water areas.
Intertuf 362 may be applied to surfaces prepared to International Paint wet abrasive blasting standard SB2, with flash rust not exceeding standard SB2M. Wet abrasive blasting is recommended only for the underwater hull, topside and above-water areas.
For maintenance, consult International Paint.
For specific advice, consult your local International Paint representative.
Note: For marine environments in North America, the following surface preparation standards may be used: SSPC-SP10 in place of Sa2.5 (ISO 8501-1:2007); SSPC-SP6 in place of Sa2 (ISO 8501-1:2007).
The coating is supplied in two containers as one unit. Always mix the entire unit in the supplied ratio. Once mixed, use within the specified pot life.
(1) Stir the base (Component A) with a power mixer.
(2) Mix all of the base (Component A) with the curing agent (Component B) and stir thoroughly with a power mixer.
International GTA220. Normally no thinning is required. Under extreme conditions, consult your local representative for application advice. Do not thin beyond the limits of local environmental regulations.
Recommended nozzle tip size 0.53–0.84 mm (21–33 thou); total fluid output pressure at the nozzle not less than 176 kg/cm² (2500 psi).
Conventional spray application is not recommended.
Brush application is recommended for small areas only. Several coats may be required to achieve the specified film thickness.
Roller application is recommended for small areas only. Several coats may be required to achieve the specified film thickness.
Do not leave paint in hoses, spray guns or spray equipment. Flush all equipment thoroughly with International thinner. Once mixed, paint should not be resealed; if work is interrupted for too long, mix a fresh batch before resuming application.
All equipment should be cleaned immediately after use with International thinner. Flushing spray equipment periodically during the day is good working practice. Cleaning frequency depends on the volume sprayed, temperature and time in use (including delays). Do not exceed the pot life of the paint.
All surplus paint and empty containers must be disposed of in accordance with appropriate local regulations/laws.
If welding or flame cutting is performed on metal coated with this product, dust and fumes will be released; use suitable personal protective equipment and local exhaust ventilation. In North America, follow the instructions in ANSI/ASC Z49.1 “Safety in Welding and Cutting”.
All work related to the application and use of this product must comply with national health, safety and environmental protection standards and regulations.
Before using this product, obtain, read and follow the health and safety information in the Material Safety Data Sheet for the product. Read and observe all precautions in the Material Safety Data Sheet and on the container label. If these warnings and requirements are not fully understood, or cannot be strictly observed, do not use the product. During application and drying of the product, provide adequate ventilation and protective measures to keep solvent vapour concentrations within safe limits, so as to prevent poisoning or oxygen deficiency. Take protective measures to avoid skin and eye contact with the product (e.g. gloves, goggles, face shield, barrier cream). Specific safety measures depend on the application method and working environment.
Emergency contact: USA/Canada — medical 1-800-854-6813; Europe — tel. (44) 191 4696111, hospital and doctor (44) 207 6359191; China — tel. (86) 532 83889090; other regions — contact the regional office.
The system of Intertuf 362 followed by Intergard 263 may be used for spot repair or upgrade on the following substrates: Spot repair (suitable substrates): - epoxy, coal tar epoxy, chlorinated rubber, vinyl tar, tar-free vinyl. Substrates not suitable for repair: - bitumen. Upgrade (suitable substrates): - epoxy, coal tar epoxy, chlorinated rubber. Substrates not suitable for upgrade: - vinyl tar, tar-free vinyl, bitumen. Feather overlap areas to a minimum.
Recoat data are for guidance only and depend on local climatic and environmental conditions. For specific advice, consult your local International Paint representative.
Apply in good weather. The temperature of the surface to be coated must be at least 3 °C above the dew point. Unless otherwise specifically instructed, raise the paint temperature to between 21 and 27 °C before mixing and application to achieve optimum application performance. Unmixed paint (in sealed containers) must be stored protectively as specified in the Storage section of this product data sheet. The technical and application data given here are intended as general guidance for establishing an application procedure. Test results are obtained in a controlled laboratory environment, and International Paint does not claim that the published test results, or any other test results, accurately represent results obtained in all site environments. Because application, environmental and design parameters vary widely, care must be exercised in coating selection, performance verification and use.
Under certain climatic conditions, especially at low temperature and high humidity, amine blooming may occur on the coating surface during drying. To prevent this, an induction time of 30 minutes between mixing and application is recommended at temperatures below 25 °C.
| Packaging Specifications | Component A | Component B | ||
| Volume | Packaging | Volume | Packaging | |
| 20 L | 15 L | 20 L | 5 L | |
| 4 US gal | 3 US gal | 5 US gal | 1 US gal | |
For other packaging sizes, consult International Paint.
| Packaging Specifications | Packaging weight |
|---|---|
| 20 L | 33.33 kg |
| 4 US gal | 56 lb |
| Shelf life | Component A - minimum 6 months at 25 °C or below. Component B - minimum 12 months at 25 °C. Re-inspection required thereafter. |
|---|
Store in a cool, dry place away from heat and ignition sources.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.
The factory item numbers for Intertuf 362 epoxy anti-corrosive paint are as follows.Item No.is the most accurate form when ordering;Colour/colour codecorresponds to the actual colour (RAL, GSB are colour chart codes);Packaging SpecificationsFactory complete-set specification format. Colors not listed may be ordered against the colour card.
| Item No. | Colour / colour code | Packaging Specifications |
|---|---|---|
| KHA323 | — | 20 L |
This model has a total of1item numbers, all listed on this page; colours outside the table (including special colours and bulk packaging) can be confirmed by phone, delivery dates are advised according to the factory's current production schedule and stock. In the packaging specification, the "+" indicates the complete-set notation for two-component products (base + curing agent), subject to the factory specification; a "—" in the colour column denotes an auxiliary product, or that the item has no colour code in the factory system.