5412A EPICON FINISH HS Epoxy Topcoat is an epoxy coating for use as a topcoat. EPICON FINISH HB is a high-build topcoat based on epoxy polyamide resin. Parameters on this page: volume solids 69 ± 2% (ISO: 3233), dry film thickness 30–100 µm, theoretical spreading rate 0.043–0.143 L/m2. Comparable products of the same brand and type: 5402C EPICON FINISH HB Epoxy Topcoat, 5402D EPICON FINISH HB EX Epoxy Topcoat, 100 EVASIGN No.100 Modified Alkyd Topcoat.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "5412A EPICON FINISH HS Epoxy Topcoat"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 69 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 30–100 µm |
| Theoretical Spreading Rate | 0.043-0.143 L/m2 |
| VOC | 331 g/L (Method 24) |
| Density / Specific Gravity | 1.42 g/ml (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPICON MARINE THINNER |
| Mixing Ratio | Base : curing agent = 75:25 (by volume) |
| Colour / Appearance | As specified colour |
EPICON FINISH HB is a high-build topcoat based on epoxy polyamide resin. It offers excellent durability and adhesion.
Its VOC is below 340 g/L.
| Type | Epoxy topcoat |
|---|---|
| Use | Can be used as an epoxy series topcoat for steel-hulled ships, bridges and other steel structures |
| Mixing Ratio | Base : curing agent = 75:25 (by volume) |
|---|---|
| Colour | As specified colour |
| Flash Point | Base 23°C Hardener 24.9°C |
| Density | 1.42 g/ml (ISO: 2811) |
| Volume Solids | 69 ± 2% (ISO: 3233) |
| Volatile organic compound content | 331 g/L (Method 24) |
| Theoretical spreading rate | 0.043-0.143 L/m2 |
| Thickness | Wet film 43–143 µm |
| Dry film | 30–100 µm |
(dry film 100 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 6 h | 4.5 h | 3 h | 2 h |
| Hard Dry | 48 h | 34 h | 20 h | 15 h | |
| Recoat interval | At least | 28 h | 20 h | 13 h | 10 h |
At most*
| Pot life | 24 h 12 h 8 h 6 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5Pa.s |
| Nozzle | Graco719, 721 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPICON MARINE THINNER |
| Thinning | 0–1% by volume |
| Preceding coat | such as UMEGUARD SX HS, UMEGUARD SX HS QD |
| Subsequent coat | - |
| Packaging | Two-component |
Note: 1. *Refer to the application specification. 2. In confined spaces or at low temperatures, ventilation is necessary to remove the volatilised solvent and promote film formation during application and film formation.
3 Excess solvent may reduce sag resistance. 4 Application is possible when the temperature drops to -5°C, but hard dry takes a long time and full cure is reached only as the temperature rises. 6 Due to the characteristics of EPICON FINISH HS epoxy coating, chalking and fading under UV exposure cannot be avoided.
7 Density, volume solids and volatile organic content are theoretical calculated values excluding thinner. These values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.