5113 EPICON ZINC HB-2 Epoxy Zinc-Rich Primer is a zinc-rich primer, in the epoxy coating system. EPICON ZINC HB-2 is a high-build anticorrosive paint based mainly on a mixture of metallic zinc, epoxy resin and curing agent; it dries quickly and has good resistance to seawater corrosion. Parameters on this page: volume solids 55 ± 2% (ISO 3233), dry film thickness 40-75 µm, theoretical spreading rate 0.073-0.136 L/m². Comparable models from the same brand: 1034 EPICON ZINC RICH PRIMER B-2 epoxy zinc-rich primer, 1036 UNIZINC 80 special epoxy zinc-rich primer, 6035 EPICON T-800 HOLDING PRIMER epoxy phenolic resin temporary anticorrosive primer.
Parameter source: CMP original technical data sheet (TDS) for 5113 EPICON ZINC HB-2 Epoxy Zinc-Rich Primer (High-Build); spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 55 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 40–75 µm |
| Theoretical Spreading Rate | 0.073-0.136 L/m2 |
| VOC | 405 g/L (Method 24) |
| Density / Specific Gravity | 2.28 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 76:24 (by volume) |
| Colour / Appearance | Grey |
EPICON ZINC HB-2 is a high-build anticorrosive paint based mainly on a mixture of metallic zinc, epoxy resin and curing agent; it dries quickly and has good resistance to seawater corrosion. It bonds with almost all types of subsequent coatings and has good resistance to heat, oil, seawater and solvents.
| Type | Epoxy zinc-rich primer (high-build) |
|---|---|
| Use | As an anticorrosive primer for steel structures |
| Mixing Ratio | Base : curing agent = 76:24 (by volume) |
|---|---|
| Colour | Grey |
| Density | 2.28 g/mL (ISO: 2811) |
| Flash Point | Base 19.5 °C Curing agent 22.5 °C |
| Volume Solids | 55 ± 2% (ISO: 3233) |
| Volatile organic compound content | 405 g/L (Method 24) |
| Theoretical spreading rate | 0.073-0.136 L/m2 |
| Thickness | Wet film 73-146 µm |
| Dry film | 40–75 µm |
()
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 30 min | 25 min | 20 min | 15 min |
| Hard Dry | 6 h | 5 h | 4 h | 3 h | |
| Recoat interval | At least | 24 h | 16 h | 8 h | |
| At most | 180 days | 180 days | |||
| Pot life | 36 h | 24 h | 12 h | 8 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 28-32 s (Ford Cup #4) |
| Nozzle | Graco612-823 |
| Paint output pressure | 8.8-11.8 Mpa |
| Spray gun speed | 80–120 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
If applied directly to steel surfaces, surface preparation to ISO Sa2½ is required; if overcoated on a primer, surface preparation to ISO St3 is required
| Preceding coat | - |
|---|---|
| Subsequent coat | BANNOH series, BISCON HB-NT L, etc. Alkyd and inorganic paints are not recommended. |
| Packaging | Two-component |
Note: 1. Waiting time required before the first cargo loading
| Temperature | 10°C | 20°C | 30°C |
| (days) | 18 | 10 | 6 |
2. Density, volume solids and volatile organic compound content are theoretical values calculated without solvent
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.