4038L ACRI 700 FINISH ST Acrylic Topcoat belongs to acrylic coatings and is used as a topcoat. ACRI 700 FINISH ST is mainly an acrylic resin-based topcoat that dries by solvent evaporation. Parameters on this page: volume solids 42 ± 2% (ISO: 3233), theoretical spreading rate 0.071–0.095 L/m², number of components single-component. Comparable products of the same brand and type: 4038G ACRI 700 FINISH G Acrylic Topcoat, 100 EVASIGN No.100 Modified Alkyd Topcoat, 2400A EVAMARINE Alkyd Topcoat.
Parameter source: CMP original technical data sheet (TDS) '4038L ACRI 700 FINISH ST Acrylic Topcoat'; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 42 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 30–40 µm |
| Theoretical Spreading Rate | 0.071-0.095 L/m2 |
| VOC | 500 g/L (Method 24) |
| Density / Specific Gravity | 1.29 g/ml (ISO: 2811) |
| Number of Components | One-component |
| Flash Point | 24.7°C |
| Thinner | CR/ACRI THINNER C |
| Colour / Appearance | White, other specified colours |
ACRI 700 FINISH ST is mainly an acrylic resin-based topcoat that dries by solvent evaporation.
It has good adhesion, weathering resistance and colour/gloss retention.
| Type | Acrylic Topcoat |
|---|---|
| Use | Topcoat for ship freeboard, waterline, deck and superstructure. |
| Colour | White, other specified colours |
|---|---|
| Flash Point | 24.7°C |
| Density | 1.29 g/ml (ISO: 2811) |
| Volume Solids | 42 ± 2% (ISO: 3233) |
| Volatile organic compound content | 500 g/L (Method 24) |
| Theoretical spreading rate | 0.071-0.095 L/m2 |
| Thickness | Wet film 71–95 µm |
| Dry film 30–40 | µm |
(dry film 35 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 2 h | 1.5 h | 1 h | 50 min | 30 min | |
| Hard Dry | 18 h | 8 h | 6 h | 5 h | 4 h | 3.5 h | |
| Recoat interval | At least | 32 h | 18 h | 12 h | 9 h | 6 h | 5 h |
At most
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 75 s (Ford cup #4) |
| Nozzle | Graco719 |
| Paint output pressure | 11.7-14.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER C |
| Thinning | 0–10% by volume |
| Preceding coat | BANNOH 500,BANNOH 200,BISCON HB-NT L,ACRI 700 PRIMER J |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
2 Below 10 °C, additional thinner may be required to achieve the desired application viscosity.
3 Excess solvent may reduce sag resistance.
4. Density and VOC content are calculated without thinner. Values may vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.